1) ferrite side plate
魏氏组织铁素体
1.
The results showed that the microstructures in CGHAZ of Ti-treated steel consisted chiefly of grain boundary ferrite,ferrite side plate and intragranular ferrite,but there were only grain boundary ferrite and ferrite side plate in CGHAZ of C-Mn steel.
结果表明,C-Mn钢焊接粗晶区主要为晶界铁素体+魏氏组织铁素体;钛处理钢焊接粗晶区主要为晶界铁素体+魏氏组织铁素体+晶内铁素体组织。
2) widmanstatten microstructure
魏氏组织
1.
Study on constitutive relationship for TC11 titanium alloy with thick laths widmanstatten microstructures deformed in two phase field;
粗片状魏氏组织TC11钛合金两相区本构关系研究
2.
The stress relaxation behavior of Ti-6Al-4V alloy with widmanstatten microstructure at 200℃, 400℃ and 600℃ were investigated, and microstructures before and after stress relaxation were observed by TEM.
利用弯曲应力松弛方法研究了魏氏组织Ti-6Al-4V合金200℃,400℃和600℃时的应力松弛行为,并利用TEM研究了应力松弛前后微观组织变化;宏观热力学参数结合微观组织观察初步探讨应力松弛机理。
3) widmanstatten structure
魏氏组织
1.
By comparing the ribbed bars with brittle fractures to the qualified rebars,it has been found that the widmanstatten structure,the rolling defects and the high inclusion are the major causes.
结果表明,魏氏组织较多、轧制缺陷及夹杂物过多是造成脆断的主要原因,并提出了相应的解决措施。
2.
The results of metallographical analysis of cracks in welding seams,show that widmanstatten structure is usually unavoidable in the welding process; however some meassures should be paid to welding failures can be taken to weliminate or minimize its influence,and attention about the easily neglected factor, that due to environment temperature change.
对焊接接头处出现的裂纹进行了金相分析,表明该部位在焊接过程中出现的魏氏组织在常规条件下是不可避免的,但是通过一些补救措施可以消除它的影响或将其影响降至最低程度,提出了环境温度的差异是造成焊接失败的因素。
3.
The results show that the appearance of Widmanstatten structure,upper bainite and martensite in the structure of 20MnSi HRB is the main cause making the yield point disappear.
结果表明 :2 0 Mn Si热轧带肋钢筋中出现的魏氏组织、上贝氏体及马氏体组织是使屈服点消失的主要原因。
5) widmanstatten sawteeth
锯齿状魏氏组织
1.
Surface relief effects associated with the widmanstatten sawteeth in an Fe-0.
37C（质量分数，％）钢中的锯齿状魏氏组织产生表面浮凸，发现其浮凸是由多片魏氏组织片条组成的浮凸群，浮凸高度约为60—170nm，低于其形核处仿晶型铁素体的表面浮凸。
6) Coarse grain widmanstatten
粗晶魏氏组织
补充资料：魏夫人
北宋女词人。即曾布妻魏氏。襄阳（今湖北襄樊）人。名字及生卒年均不详，生平亦无可考。曾布参与王安石变法，后知枢密院事，为右仆射，魏氏以此封鲁国夫人。弟魏泰，著有《临汉隐居诗话》、《东轩笔录》。她的词多写离情别绪，如〔好事近〕："不堪西望去程赊，离肠万回结"；〔菩萨蛮〕："何处是离愁，长安明月楼。"这大约与曾布在吕惠卿、章惇、蔡京先后当政时多次贬谪在外有关。目睹身受，因此她笔下的离愁别恨表现得颇为深沉真切。如〔阮郎归〕从"夕阳楼外落花飞"写到"孤烟卷翠微"，以春归日暮反托出"归来未有期"的怅惘，又结以"桐阴月影移"，着意渲染"断魂不忍下危梯"的悽惋。这是在一般融情入景之外，再从内心抒发上更进一层。魏夫人的词不仅表现一己的幽愁暗恨，也还有"荷花娇欲语，笑入鸳鸯浦"（〔菩萨蛮〕）这类轻快活泼的篇章，能够生动地描绘出采菱女子的劳动与爱情生活。
魏夫人的文学创作在宋代颇负盛名，朱熹甚至将她与李清照并提（《词综》卷二十五）。但她的作品留下的只有诗 1首，咏项羽、虞姬事，题作《虞美人草行》(《诗话总龟》卷二十一)；词10余首，周泳先辑为《鲁国夫人词》。
魏夫人的文学创作在宋代颇负盛名，朱熹甚至将她与李清照并提（《词综》卷二十五）。但她的作品留下的只有诗 1首，咏项羽、虞姬事，题作《虞美人草行》(《诗话总龟》卷二十一)；词10余首，周泳先辑为《鲁国夫人词》。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条