1) quasi-single phase ferrite
准单相铁素体组织
1.
The experimental results have shown that the quasi-single phase ferrite matrix micro-structure can be obtained by isothermal holding between 650℃ and 750℃ after deformation, and the pearlite could be eliminated.
结果表明,变形后在650-750℃等温100 s时可获得准单相铁素体组织从而基本消除珠光体组织。
2) single phase ferrite
单相铁素体组织
3) quasi-acicular ferrite
准针状铁素体组织
1.
Based on spike height resulting in break marks,the new technique of eliminating break marks by getting microstructure of quasi-acicular ferrite in hot strip mill was applied.
结果表明:产生横折缺陷存在临界的上下屈服点应力差,准针状铁素体组织可降低上下屈服点应力差,并使其低于这个临界值,更为重要的是,准针状铁素体组织使控制横折缺陷的工艺难度大大降低;钢中碳含量高、奥氏体晶粒粗、加速冷却速度快、加速冷却开始和结束温度低,有利于获得准针状铁素体组织,最佳的加速冷却开始和结束温度分别为先共析铁素体和珠光体开始转变温度。
5) ferrite side plate
魏氏组织铁素体
1.
The results showed that the microstructures in CGHAZ of Ti-treated steel consisted chiefly of grain boundary ferrite,ferrite side plate and intragranular ferrite,but there were only grain boundary ferrite and ferrite side plate in CGHAZ of C-Mn steel.
结果表明,C-Mn钢焊接粗晶区主要为晶界铁素体+魏氏组织铁素体;钛处理钢焊接粗晶区主要为晶界铁素体+魏氏组织铁素体+晶内铁素体组织。
6) Ferrite Strip Structure
铁素体带状组织
补充资料：低温铁素体钢
分子式：
CAS号：
性质：适合低温(273～153K)使用的低合金铁素体钢。它们在脆性转变温度以上使用。可为三类：(1)低碳-锰钢，如233K用钢16Mn属于此类；(2)低镍钢，在233～213K用0.5％Ni钢；当温度降至193～183K时，用2.25％Ni钢，或含锰的1.5％Ni钢；(3)无镍铬低温铁素体钢，主要有203K用钢09Mn2V及09MnTiCuRE，183K用钢06MnNb，153K用钢06AlCu和06AlNbCuN。低温铁素体钢主要用于液体丙烷与丙烯、液氨等液化气的储存及输送装置，寒冷地区野外作业的设备和工程结构以及一些冷冻设备等。
CAS号：
性质：适合低温(273～153K)使用的低合金铁素体钢。它们在脆性转变温度以上使用。可为三类：(1)低碳-锰钢，如233K用钢16Mn属于此类；(2)低镍钢，在233～213K用0.5％Ni钢；当温度降至193～183K时，用2.25％Ni钢，或含锰的1.5％Ni钢；(3)无镍铬低温铁素体钢，主要有203K用钢09Mn2V及09MnTiCuRE，183K用钢06MnNb，153K用钢06AlCu和06AlNbCuN。低温铁素体钢主要用于液体丙烷与丙烯、液氨等液化气的储存及输送装置，寒冷地区野外作业的设备和工程结构以及一些冷冻设备等。