1) corrosion scale
腐蚀产物膜
1.
Influence of CO_2 partial pressure on the protection property of corrosion scale formed on N80 steel;
CO_2分压对N80钢腐蚀产物膜保护性能的影响
2.
Formation mechanism of corrosion scales of carbon steel by CO_2 corrosion under high temperature and high pressure;
碳钢高温高压CO_2腐蚀产物膜的形成机制
3.
Effect of temperature and pressure on profile of C0_2 corrosion scales on oil well steels;
CO_2腐蚀产物膜形态结构与温度和压力的关系
2) corrosion product film
腐蚀产物膜
1.
The spalling of corrosion product film would accelerate the galvanic corrosi.
结果表明在H_2S/CO_2饱和的3%NaCl溶液中电偶腐蚀与浸泡腐蚀产物基本相同,腐蚀产物膜的脱落直接导致电偶腐蚀速率的剧增。
2.
The corrosion product films are loose, average corrosion rate is high, and there is slight local corrosion that has h.
用失重法、扫描电镜(SEM)、能谱分析(EDS)及X射线能谱(XRD)对N80S抗硫油管钢在CO2、微量H2S及高浓度Cl-条件下的腐蚀破坏进行腐蚀实验研究,结果发现,在实验条件下,微量H2S的存在对反应系统影响较大;在膜的形成过程中硫化物腐蚀产物膜(FeS、FeS0。
3.
The morphology of sulfate-reducing bacteria(SRB),microbial biofilms,corrosion product film and corroded A3 steel have been observed by atomic force microscopy(AFM).
应用原子力显微镜(AFM)研究硫酸盐还原菌(SRB)、微生物膜、腐蚀产物膜和A3钢腐蚀后的表面形貌,获得了高分辨率、清晰的图像。
3) corrosion product scale
腐蚀产物膜
1.
Polarization resistance measurement,electrochemical impedance spectroscopy(EIS) and SEM observation were used to investigate the effect of calcium ions on the formation process and the protective performance of the corrosion product scale on NC-55E steel during CO2 corrosion at 80℃.
通过线性极化、电化学阻抗谱测试和SEM观察,研究了80℃条件下Ca2+浓度对NC-55E套管钢CO2腐蚀产物膜的形成过程及其保护性能的影响。
2.
In the CO2 corrosion process,the corrosion product scale will be formed on the steel surface,providing protection for the steel or changing its morphology and mechanical properties.
在模拟油田CO2腐蚀环境下,利用失重法、极化曲线及交流阻抗技术研究了X65钢在不同腐蚀时间和不同温度下形成的腐蚀产物膜特征。
3.
An autoclave was employed to prepare CO_2 corrosion product scales on N80 steel.
在高温高压静态釜的模拟油田采出液中用N80钢制取了CO2腐蚀产物膜,用扫描电镜测定了膜表面晶粒大小和厚度并分别观察了腐蚀膜磨损前后的形貌特征,利用自制的磨损装置对比分析了在水砂两相介质中膜的磨损性能与成膜温度、膜层形貌和结构、流速及砂粒度之间的关系。
4) corrosion product scales
腐蚀产物膜
1.
The images and chemical composing of corrosion product scales were got according to the research and analysis of SEM, EDS, XPS.
针对N80钢的CO2腐蚀性能,模拟大庆油田井下的腐蚀环境,通过高温高压釜进行了N80钢的腐蚀实验,采用SEM、EDS和XPS测试手段分析研究所获得的CO2腐蚀产物膜的形貌和化学组成。
2.
the images and chemical composing of corrosion product scales were got according to the research and analysis of SEM,XRD.
针对N80钢的CO2腐蚀性能,模拟大庆油田井下的腐蚀环境,通过高温高压釜进行了N80钢的腐蚀实验,采用SEM、XRD分析研究所获得的CO2腐蚀产物膜的形貌和化学组成。
5) corrosion scales
腐蚀产物膜
1.
Effect of CO_2 partial pressure on corrosion scales of tubular steels;
CO_2分压对油管钢腐蚀产物膜的影响
2.
While simulating the CO 2 corrosion environment in oilfield,the characteristics of CO 2 corrosion scales on 1%Cr-containing N80 steel were studied.
在模拟油田CO2 腐蚀环境下 ,研究了含 1%Cr的N80钢腐蚀产物膜的特征 。
6) CO2 Corrosion Scale
CO2腐蚀产物膜