1) iron corrosion products
铁腐蚀产物
1.
The iron corrosion products produced by the reduction reaction between iron and nitrate under different pH were studied.
结果表明:腐蚀产物的主要成分是Fe3O4和FeO(OH),随反应体系初始pH值的降低,Fe3O4的比例逐渐增大;腐蚀产物表面呈多孔疏松结构,对Fe2+具有一定的吸附作用,可在一定程度上促进铁粉对硝酸盐的还原;铁腐蚀产物的形成总体上降低了铁对硝酸盐的还原效果,较低pH值条件下形成的铁腐蚀产物对硝酸盐去除效果的影响较小。
2) corrosion product
腐蚀产物
1.
Appearance and formation process of corrosion products on archaeological iron in simulated soil media;
模拟土壤介质中仿古铸铁腐蚀产物的形貌及其生长过程
2.
Co-precipitation of nano-crystalline corrosion products on hot dip Zn-Al alloy coating;
热浸锌铝合金镀层表面纳米晶腐蚀产物共沉积机理
3) Corrosion products
腐蚀产物
1.
Corrosion behavior and corrosion products of a low carbon bainite steel in three kinds of typical environments
低碳贝氏体钢在三种典型环境中的腐蚀行为和腐蚀产物
2.
The polarization curves of zinc alloy anodes in Ca(OH)2 solutions have been measured by potentiodynamic method,and the composition of corrosion products were examined by X-ray-diffraction(XRD).
应用恒电位法测定锌合金阳极在不同pH值的Ca(OH)2溶液中的极化曲线,X-射线衍射分析了该锌合金阳极的腐蚀产物。
3.
The corrosion products, tubular goods and water supply in Zhongyuan oilfield are analyzed.
采用XRD、EPMA和SRB检测对中原油田套管腐蚀产物进行分析 ,并试验了碳钢在含CO2 介质中的腐蚀 ,研究结果表明 ,CO2 及高矿化度产出水是套管腐蚀失效的主要原因 ,套管钢材中夹杂物的局部分布及流体冲刷是加剧油套管局部腐蚀穿孔破坏的另一原
4) corrosion product scale
腐蚀产物膜
1.
Polarization resistance measurement,electrochemical impedance spectroscopy(EIS) and SEM observation were used to investigate the effect of calcium ions on the formation process and the protective performance of the corrosion product scale on NC-55E steel during CO2 corrosion at 80℃.
通过线性极化、电化学阻抗谱测试和SEM观察,研究了80℃条件下Ca2+浓度对NC-55E套管钢CO2腐蚀产物膜的形成过程及其保护性能的影响。
2.
In the CO2 corrosion process,the corrosion product scale will be formed on the steel surface,providing protection for the steel or changing its morphology and mechanical properties.
在模拟油田CO2腐蚀环境下,利用失重法、极化曲线及交流阻抗技术研究了X65钢在不同腐蚀时间和不同温度下形成的腐蚀产物膜特征。
3.
An autoclave was employed to prepare CO_2 corrosion product scales on N80 steel.
在高温高压静态釜的模拟油田采出液中用N80钢制取了CO2腐蚀产物膜,用扫描电镜测定了膜表面晶粒大小和厚度并分别观察了腐蚀膜磨损前后的形貌特征,利用自制的磨损装置对比分析了在水砂两相介质中膜的磨损性能与成膜温度、膜层形貌和结构、流速及砂粒度之间的关系。
5) corrosion product film
腐蚀产物膜
1.
The spalling of corrosion product film would accelerate the galvanic corrosi.
结果表明在H_2S/CO_2饱和的3%NaCl溶液中电偶腐蚀与浸泡腐蚀产物基本相同,腐蚀产物膜的脱落直接导致电偶腐蚀速率的剧增。
2.
The corrosion product films are loose, average corrosion rate is high, and there is slight local corrosion that has h.
用失重法、扫描电镜(SEM)、能谱分析(EDS)及X射线能谱(XRD)对N80S抗硫油管钢在CO2、微量H2S及高浓度Cl-条件下的腐蚀破坏进行腐蚀实验研究,结果发现,在实验条件下,微量H2S的存在对反应系统影响较大;在膜的形成过程中硫化物腐蚀产物膜(FeS、FeS0。
3.
The morphology of sulfate-reducing bacteria(SRB),microbial biofilms,corrosion product film and corroded A3 steel have been observed by atomic force microscopy(AFM).
应用原子力显微镜(AFM)研究硫酸盐还原菌(SRB)、微生物膜、腐蚀产物膜和A3钢腐蚀后的表面形貌,获得了高分辨率、清晰的图像。
6) corrosion scale
腐蚀产物膜
1.
Influence of CO_2 partial pressure on the protection property of corrosion scale formed on N80 steel;
CO_2分压对N80钢腐蚀产物膜保护性能的影响
2.
Formation mechanism of corrosion scales of carbon steel by CO_2 corrosion under high temperature and high pressure;
碳钢高温高压CO_2腐蚀产物膜的形成机制
3.
Effect of temperature and pressure on profile of C0_2 corrosion scales on oil well steels;
CO_2腐蚀产物膜形态结构与温度和压力的关系
补充资料：腐蚀产物
分子式：
CAS号：
性质： 腐蚀过程生成的产物。包括：(1)腐蚀过程中发生化学作用时，在金属表面直接生成的产物；(2)随着腐蚀过程的进行，由于靠近金属表面的液层中组分变化引起的次生反应所产生并黏附在金属表面的产物。这些腐蚀产物往往成膜覆盖在金属表面，而腐蚀过程的许多特点与膜的性质变化有关。致密的膜，对金属有保护性，而疏松的膜，可能促进腐蚀。
CAS号：
性质： 腐蚀过程生成的产物。包括：(1)腐蚀过程中发生化学作用时，在金属表面直接生成的产物；(2)随着腐蚀过程的进行，由于靠近金属表面的液层中组分变化引起的次生反应所产生并黏附在金属表面的产物。这些腐蚀产物往往成膜覆盖在金属表面，而腐蚀过程的许多特点与膜的性质变化有关。致密的膜，对金属有保护性，而疏松的膜，可能促进腐蚀。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条