1.
Investigation on Elements Responsible for Development of External Surface Cracks of Drill Pipe Body in Steel X95
X95钢级钻杆管体外表面裂纹形成原因分析
2.
External defects: undercut,overip,arc pit, gas cavity in surface,crack in surface.
外部缺陷：咬边、焊瘤、弧坑、表面气孔、表面裂纹。
3.
ON THE FORMATION MECHANISM OF INTERNAL AND SURFACE CRACKS OF CONTINUOUSLY CAST SIABS
连铸板坯内部裂纹和表面裂纹的形成机理
4.
No stress measurements or crack surface samples were available for examination, only the surface crack configuration.
没有应力测量或裂纹表面取样可用于检验，只能依据表面裂纹图形。
5.
Effects of the Surface Perturbation and the External Stress on the Evolutons of Microcracks;
裂面形貌扰动和外载对微裂纹演变的影响
6.
To cause(china, for example) to become covered with a network of fine cracks.
使（瓷器等）表面出现网状的细裂纹
7.
glazed china with a network of fine cracks on the surface.
表面有网状裂纹的光滑的瓷器。
8.
Cracks grow in directions nearly parrallel to the surface.
裂纹在近乎平行于表面的方向上生长。
9.
A core was removed from this area so that the crack surfaces could be examined.
从这一区域取样芯，以便检验裂纹表面。
10.
BEM Analysis of Transient Response in Surface Crack Problems
表面裂纹问题瞬态响应的边界元分析
11.
The Remaining Strength Assessment of Pipeline Containing 360°Cir- cumferential Surface Crack,
含360°表面裂纹管道剩余强度评价
12.
Analyses of cause for transverse cracks on CC slab surface
连铸板坯表面横向裂纹产生原因分析
13.
Study On Longitudinal Surface Cracks On CSP Hot-Rolled Plate
酒钢CSP热轧板卷表面纵裂纹研究
14.
Surface Network Cracks in Low Carbon Boron Steel Casting
低碳硼合金钢表面网状裂纹成因分析
15.
Thermal-elastic Fracture of Hollow Cylinder with a Semi-elliptic Surface Crack
含表面裂纹圆柱壳体的热力耦合效应
16.
ANALYSIS ABOUT NET-SHAPE CRACKS ON THE SURFACE OF A350 LF6 CONTINUOUS CASTING BILLET
A350 LF6连铸坯表面网状裂纹分析
17.
Analysis on Reasons of Surface Cracks Formation of S355 Round Tube Blank and Corresponding Countermeasures Taken
S355圆管坯表面裂纹成因及解决对策
18.
CAUSE ANALYSIS FOR SURFACE LONGITUDINAL CRACKS ON Q235B SLAB
Q235B钢板坯表面纵裂纹的原因分析