1.
The smaller the curvature and the larger the crack length the smaller will be the fracture stress.
曲线半径越小，裂纹长度越大，断裂应力也就越低。
2.
An Objective Amount for Describing lnitial Crack Length at the Notch Root
一种描述缺口根部初始裂纹长度的客观量
3.
That is, the load is dropped off in the proportion to the crack length.
这就是说，载荷随裂纹长度的增加而按比例地下降。
4.
The effect of these nonlinearities can be avoided by determining compliance at the same maximum load for all crack lengths investigated.
这些非线性效应，可在测定所有裂纹长度的柔度方法时，采用最大载荷不变的方法予以消除。
5.
Sub-critical crack growth length of shear (Mode Ⅱ) fracture of rock
岩石剪切亚临界裂纹扩展长度的研究
6.
Crack- A mark found on a wafer that is greater than0.25 mm in length.
裂纹-长度大于0.25毫米的晶圆片表面微痕。
7.
Relationship between Surface Length and Inside Length of Fatigue Crack in Ultra-high Strength Steel
航空用超高强度钢疲劳裂纹表面长度与内部长度之间的关系
8.
In the paper, mainiy discusses character of crack of high hardness hardfacing layer( HRC62 over), its growing period and adopting technology measure to prevent from producing of crack.
文章主要讨论了高硬度堆焊层裂纹的特征、长时期以及防止裂纹产生的工艺措施。
9.
Dynamic Split Tension Strength of Marble and the Properties of Crack Initiation and Crack Propagation under Dynamic Split Tests;
大理岩动态劈裂拉伸强度和裂纹起裂扩展特性
10.
Cracks grow in directions nearly parrallel to the surface.
裂纹在近乎平行于表面的方向上生长。
11.
Crack propagation usually begins slowly.
裂纹的增长常常是开始缓慢。
12.
High environment humidity increases the susceptibility to hy-drogen induced cracking and stress corrosion cracking.
高湿度能增大氢致裂纹和应力腐蚀开裂倾向。
13.
Standard test method for surface-crack fracture toughness Kle of metallic plates
GB/T7732-1987金属板材表面裂纹断裂韧度Kle试验方法
14.
FRACTURE TOUGHNESS MEASUREMENT OF CAST MAGNESIUM ALLOY BY CYLINDRICAL SPECIMEN WITH RING-SHAPED CRACK
用环状裂纹圆柱试样测定铸镁合金的断裂韧度
15.
Multi-scale Analysis of Mechanical Properties on Fracture Process Zone
多尺度下裂纹断裂过程区力学特性分析
16.
Prediction of Burst Strength of Oil Well Casing Strings with Micro-Cracks
含微裂纹油井套管的抗内压断裂强度预测
17.
Fracture Strength of Wires with Cracks in Suspension Bridge
带裂纹的悬索桥主缆钢丝的断裂强度分析
18.
STUDY OF THE CRITICAL TEMPERATURES FOR DELAYED HYDRIDE CRACKING IN N18 ZIRCONIUM ALLOY
N18锆合金氢致裂纹延迟开裂临界温度研究