1) cyclic spheroidizing annealing
周期球化退火
1.
Effect of cyclic spheroidizing annealing on microstructure and mechanical properties of GCr15 bearing steel
周期球化退火对GCr15轴承钢组织及力学性能的影响
2) annealing period
退火周期
1.
The effect of the rare earth compound inoculant on graphitizing the annealing period of the malleable cast-iron was studied and analyzed.
配制了以稀土元素为主的可锻铸铁复合孕育剂，进行了生产实验，研究和分析了稀土复合孕育剂对可锻铸铁石墨化退火周期的影响。
3) periodic annealing
周期退火
4) annealing cycle
退火热周期
1.
1 CGL and also describes the application of several energy saving technologies in annealing furnace,such as no water cooling furnace bottom roll,low thermal capacity refractory fiber material,residual heat reuse,annealing cycle and combustion sequence control.
介绍了冷轧薄板厂1号镀锌线退火炉的基本结构和工艺过程;阐述了在退火炉上应用无水冷炉底辊、低热容耐火纤维结构、余热利用、退火热周期、次序燃烧控制等节能技术的基本情况。
5) spheroidal annealing
球化退火
1.
Production of spheroidal annealing of cold rolled 25 steel strip;
25钢冷轧球化退火钢带的生产
2.
To introduce a new process for making needle latch steel wire with diameter range 0 34～0 53mm The technological process consists of patenting-phosphating-cold drawing-spheroidal annealing under Ac 1 point in electrical heating furnace-slight drawing to finished product The theoretical basis and advantages of the main points of new process are emphatically elaborate
该工艺流程是：铅淬火—磷化—拔丝—Ａｃｌ以下电加热连续退火炉球化退火—轻拉至成品。
6) spheroidizing annealing
球化退火
1.
In order to solve the problem of crack deformation tendency of the quenched steel wires for a uniform structure,development is done to the special wire of hi-carbon and low alloy,finding that there is variation of spheroidizing annealing processed structure under the same spheroidizing annealing process once drawed.
为了改善针布齿条淬火时的变形开裂倾向性,使其最终性能均匀,研究了针布齿条专用高碳低合金钢丝经过不同程度拉拔变形后,在相同球化退火工艺下具有差异的球化退火组织,并且比较了经较大拉拔变形后钢丝退火前后的组织差异,以及该钢丝经轧制前后的组织变化情况。
2.
The carbide morphology and distribution in the microstructure of 4Cr10Si2Mo steel have been improved through the improvement of spheroidizing annealing proce.
通过改进球化退火工艺,使4Cr10Si2Mo钢的显微组织中的碳化物形态、分布得到改善,气门电镦的质量有了明显的提高。
3.
The effects of rolling process on spheroidizing annealing of GCr15 were studied by thermo-simulation.
通过热模拟的方法研究轧制工艺对GCr15球化退火的影响。
补充资料：软化退火(见低温退火)
软化退火(见低温退火)
soft-annealing
rU0nhUO tUihUO软化退火(soft一annealing)见低温退火。