2) three-dimensional ordered porous film
三维有序多孔膜
3) three dimensional porous material
三维有序多孔材料
4) 3DOM
三维有序大孔
1.
Three-dimensionally ordered macroporous SiO_2 materials(3DOM SiO_2) were successfully synthesized by using colloid crystal template which was assembled by sedimentation of polystyrene microsphere.
以聚苯乙烯微球(polystyrenemicrosphere)自然沉积形成的胶体晶体作模板,将以正硅酸甲酯制备的SiO2溶胶填充到模板间隙中,原位形成凝胶,最后通过焙烧除去模板,得到三维有序大孔SiO2。
2.
Three dimensional ordered macroporous (3DOM) zirconium dioxides with pore diameters of about 500 nm are successfully prepared via a direct calcining step, using a methanol solution of ZrOCl2·8H2O as filling precursor and polystyrene sphere (PS) colloid crystals as templates.
以聚苯乙烯微球胶晶为模板,氧氯化锆的甲醇溶液为前驱物,通过直接热分解的方法制备了三维有序大孔氧化锆(3DOM-ZrO2);利用SEM、TEM、EDS和BET等技术对其进行了表征,并探讨了实验条件对大孔结构与形态的影响。
5) 3D-ordered porous material
三维有序孔材料
6) ordered porous
有序多孔
1.
Tin-doped ordered porous zirconium oxides are successfully synthesized by co-precipitation method using zirconyl chloride and tin chloride as Zr/Sn sources and octadecyltrimethylammonium bromide(C18TAB)as template.
以C18TAB为模板剂,氧氯化锆和四氯化锡为原料,采用共沉淀法成功合成了不同掺锡量的有序多孔氧化锆。
补充资料：多孔膜
分子式：
CAS号：
性质： 指每平方厘米含有一千万至一亿个孔，孔隙率占总体积70％～80％，孔径均匀，孔径范围在0.02～20μm之间的分离膜。当膜的孔径大于5nm时称为微孔膜(microporous membrane)；孔径在1～5nm时称细孔膜(fine-pored membrane)，包括超滤膜和反渗透膜。
CAS号：
性质： 指每平方厘米含有一千万至一亿个孔，孔隙率占总体积70％～80％，孔径均匀，孔径范围在0.02～20μm之间的分离膜。当膜的孔径大于5nm时称为微孔膜(microporous membrane)；孔径在1～5nm时称细孔膜(fine-pored membrane)，包括超滤膜和反渗透膜。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。