1) Monomer Casting Nylon 6
铸型尼龙6(MC尼龙6)
2) MC nylon 6
MC尼龙6
1.
Non-isothermal Crystallization Kinetics of Silica/MC Nylon 6 In-situ Nano-scale Composites;
纳米二氧化硅/MC尼龙6原位复合材料非等温结晶动力学的研究
2.
Study of discrete relaxation time spectrum of MC nylon 6/Kevlar fiber compos-ite melts;
MC尼龙6/Kevlar纤维复合材料松弛时间谱的计算研究
3.
A new method of synthesizing carbon fiber(CF,whose surface is grafted by nylon 6)/MC nylon 6 in-situ composites is proposed and the composites are characterized.
提出一种表面接枝尼龙6的碳纤维/MC尼龙6原位复合材料的制备方法并加以表征。
3) MC Nylon6
MC尼龙6
1.
Non-isothermal crystallization kinetics of Silica /MC nylon6 In Situ Nanocomposites
纳米二氧化硅/MC尼龙6原位复合材料非等温结晶动力学
2.
In this thesis, after homogeneously dispersing nano-silica in ε -caprolactam melt, silica/MC nylon6 in-situ nanocomposites possessing evenly dispersed silica were successfully obtained via anionic polymerization.
本工作将纳米SiO_2均匀分散在己内酰胺熔体中，通过阴离子聚合法制备了纳米粒子均匀分散的纳米SiO_2／MC尼龙6原位复合材料。
4) MC PA6
铸型尼龙6
5) MCPA6
浇铸尼龙6
1.
MCPA6/PP0 (95/5) blend was prepared by means of in-situ blending, in which Na-MMT was dispersed with the help of water.
采用水辅助分散钠基蒙脱土(Na-MMT)通过原位共混的方法制备了浇铸尼龙6(McPA6)和聚苯醚(PPO)共混物(95/5)。
6) star shaped nylon 6
星型尼龙6
补充资料：铸型尼龙
分子式：
CAS号：
性质：亦称铸型尼龙(cast nylon)。将己内酰胺(或其他内酰胺)熔融后加入催化剂和助催化剂，迅速均匀浇铸于预热的模具内，在惰性气体环境中使之开环聚合制得的浇铸制品。熔点198℃，拉伸强度75～97MPa，拉伸弹性模量240～310MPa，压缩强度96～104MPa，弯曲强度>95MPa，冲击强度(缺口)约5kJ/m2，洛氏硬度R95～120，热变形温度(0.45MPa)204～218℃。主要用于尼龙大型制品，少量多品种制品，如制作滑动轴承、齿轮、大型阀座、导轨、容器等。
CAS号：
性质：亦称铸型尼龙(cast nylon)。将己内酰胺(或其他内酰胺)熔融后加入催化剂和助催化剂，迅速均匀浇铸于预热的模具内，在惰性气体环境中使之开环聚合制得的浇铸制品。熔点198℃，拉伸强度75～97MPa，拉伸弹性模量240～310MPa，压缩强度96～104MPa，弯曲强度>95MPa，冲击强度(缺口)约5kJ/m2，洛氏硬度R95～120，热变形温度(0.45MPa)204～218℃。主要用于尼龙大型制品，少量多品种制品，如制作滑动轴承、齿轮、大型阀座、导轨、容器等。