1) large size extruding bar
![点击朗读](/dictall/images/read.gif)
大规格挤压棒材
1.
Research of process for 6061 aluminum alloy large size extruding bar
![点击朗读](/dictall/images/read.gif)
6061铝合金大规格挤压棒材生产工艺的研究
2) large-size extrusion plate
![点击朗读](/dictall/images/read.gif)
大规格挤压板材
1.
In production of 6061-T6511 alloy large-size extrusion plates,the grain was coarse and the mechanical performance couldn\'t attain the required standards.
从生产6061-T6511铝合金大规格挤压板材晶粒粗大、力学性能不达标入手,分析了其缺陷产生及力学性能不合格的原因,提出了相应的解决措施,满足了生产的需要。
3) large-scale bar
![点击朗读](/dictall/images/read.gif)
大规格棒材
1.
The main influence factors of mechanical property of 6082T6 large-scale bars are analyzed by test and research.
通过试验研究,分析了6082T6大规格棒材力学性能的主要影响因素,并指出热处理工艺是影响6082T6大规格棒材力学性能的关键因素,棒材力学性能偏低的主要原因是生产中加热保温时间不足够长所致。
4) hot~extruded rods
![点击朗读](/dictall/images/read.gif)
热挤压棒材
5) Φ300mm hot extrusion bar
![点击朗读](/dictall/images/read.gif)
Φ300mm热挤压棒材
1.
Through analyze on mechanical property, chemical composition, metallurgical structure observation, SEM observation, spectrum analyze, microstructure and mechanical property on of Φ300mm hot extrusion bar of 2024-T4 is detected.
通过使用力学性能检测、化学成分分析、金相显微镜观察、扫描电镜观察、能谱分析等手段,检测分析了国产2024T4Φ300mm热挤压棒材微观组织和力学性能。
6) extruded hollow bar
![点击朗读](/dictall/images/read.gif)
挤压空心棒材
补充资料:变断面型材挤压
变断面型材挤压
extrusion of variable cross section shapes
b ianduanmian xjngeai Jiya变断面型材挤压(extrusion of variable。rossseetion shapes)用挤压法生产断面变化的型材,有阶段变断面型材和逐渐变断面型材之分,主要用作结构材料,它们的挤压方法也有所不同。 阶段变断面型材的挤压方法有双位楔法和可拆卸模法两种: (1)双位楔法(图1)。在型材前端经第1模成形挤压后,松开压紧楔,后端部分用第2模挤压.氯篡嘟豁 图1双位楔法挤压阶段变断面型材 1一压紧楔;2一第1模;3一第2模 (2)可拆卸模法。可拆卸模由3~4个模块组成。首先将小断面的可拆卸模装在模支承中并移至桥压筒进行挤压。挤压完毕后,移开模支承,同时,将模子同型材和模支承脱开,换上可挤压大断面型材的可拆卸模,并将模支承再移至挤压筒进行挤压。 逐渐变断面型材的挤压方法有可移动模法和带锥度异形针法两种. (D可移动模法(图2)。在挤压过程中,活动模块借助于仿形尺的作用改变位置(上升或下降),从而逐渐改变模孔的形状和尺寸,挤出逐渐变断面型材。臀 图2可移动模法挤压逐渐变断面型材 1一不动模;2一活动模块;3一保护环;4一挤压筒;5一仿形尺 (2)带锥度异形针法。采用带有锥度的异形针和相应的异形模挤压。 (王祝堂)