1) SBR latex modified cement mortar
SBR乳液改性水泥砂浆
4) modified cement mortar
改性水泥砂浆
1.
The SA modified cement mortar, which offers excellent performance in cohesion, anti - permeation, wearing resistance and chemical corrosion resistance etc, is a good new material for repairing concrete surface.
SA改性水泥砂浆具有优异的粘结、防渗、耐磨、耐化学介质腐蚀等性能,是一种新型混凝土表面修补护面材料。
2.
The effects of mass ratios of polybutadiene to styrene and the polymer-cement ratios on the flow,water reduction effect,water retention rate,compressive and flexural strengths and water absorption rate of PB-g-PS latex modified cement mortar were examined, then the performance of the carboxyl SBR latex-modified cement mortar was compared.
在固定流动度为(175±5)mm,且在20℃水中养护6 d,然后在20℃,相对湿度为65%的空气中养护21 d的混合养护条件下,考察了聚灰比、聚丁二烯与聚苯乙烯的质量比对PB-g-PS胶乳改性水泥砂浆的水灰比、流动度、保水率、抗压和抗折强度以及吸水量的影响,并与羧基丁苯胶乳改性水泥砂浆进行了性能对比试验。
5) cement mortar modifier
水泥砂浆改性剂
6) modified cement grout
改性水泥浆液
补充资料:SBR
丁苯橡胶是以丁二烯与苯乙烯为单体.通过乳液或溶液聚合而制得的共聚弹性体, 数均分子量约为(1.5-4)×105,重均分子量见约为(2-10)×105。乳液聚合丁苯橡胶简称乳聚丁苯橡胶,丁二烯和苯乙烯两种单体链节在共聚物大分子中呈无规分布。丁二烯的加成反应80%发生在1,4位置.约20%在1,2位置。其中1,4位上的链节又有顺式和反式两种构型。此外,还有少量支化和交联结构存在。乳聚丁苯橡胶的性质受结合苯乙烯量、聚合温度及乳化剂种类等的影响。通用的丁苯橡胶结合苯乙烯为(23.5)%,冷法(5℃)聚合,松香酸皂或脂肪酸皂为乳化剂。玻璃化温度Tg=-57~-52℃。早期乳聚丁苯橡胶的名称是由德国的丁钠橡胶(Buna)演变而来,称为Buna-S.美国则称为GR-S,l 961年以后统称为SBR,采用数字系列代表乳聚丁苯橡胶的品种和牌号,
1000系列 热法聚合无填料丁苯胶
1100系列 热法聚合充炭黑母炼胶;
1200系列 热法聚合充油母炼胶;
1300系列 热法聚合充油炭黑母炼胶
1500系列 热法聚合无填料丁苯橡胶
1600系列 热法聚合充炭黑母炼胶;
1700系列 冷法聚合充油橡胶;
1800系列 冷法聚合充油亢炭黑母炼胶
1900系列 其他丁苯橡胶。
丁苯橡胶具有良好的耐热性、耐磨性、耐老化性,耐油性和耐臭氧性较差。贮存稳定性较好,在阴暗处贮存期可达数年之久。丁苯橡胶的溶解度参数δ=8.5-8.6,溶于苯、甲苯、醋酸乙酯、氯仿等。