1) CM140B
氯化聚乙烯橡胶(CM140B)
1.
The filling effect of nanokaolin to the CM140B was researched.
研究了纳米高岭土对氯化聚乙烯橡胶(CM140B)的填充补强作用。
2) CM
氯化聚乙烯橡胶
1.
Effect of magnesium hydroxide on properties of CM;
氢氧化镁对氯化聚乙烯橡胶性能的影响
2.
The effects of the CM/RIIR blending ratio on the properties of CM/RIIR blend were investigated.
研究氯化聚乙烯橡胶(CM)/IIR再生胶(RIIR)并用比对CM/RIIR并用胶性能的影响。
3) chlorinated polyethylene rubber
氯化聚乙烯橡胶
1.
The properties, compounding and application of chlorinated polyethylene rubber were developed briefly.
简要介绍了氯化聚乙烯橡胶的性能、配合加工及应
2.
The cable jacket with flame and oil resistance based on chloroprene rubber(CR)/ chlorinated polyethylene rubber(CPE)was developed.
在氯丁橡胶(CR)/氯化聚乙烯橡胶(CPE)素炼时,加入2～3份具有高润滑作用的饱和脂肪酸酯型均化剂和10～12份中等相对分子质量的合成酯类增塑剂,能改善氧化锌、氧化镁在橡胶中的分散性,提高胶料的流动性、阻燃性和加工工艺性能。
4) vulcanization of chlorosulfonated Polyethylene rubber
氯磺化聚乙烯橡胶硫化
5) CSM
氯磺化聚乙烯橡胶
1.
After comparing the features of many special purpose rubber,CSM is selected as main material of rubber electrode plate.
本文从实用角度对比了多种橡胶特性、最后选定氯磺化聚乙烯橡胶作为研制船形橡胶极板的主体材料。
6) chlorinated polyethylene blended with rubber
氯化聚乙烯橡胶共混
补充资料：氯化聚乙烯
氯化聚乙烯是由聚乙烯与氯气通过取代反应而制的改性高聚物，简称CPE。随着氯的取代，破坏了聚乙烯的结晶性，使玻璃化温度降低，但超过一定的氯含量之后，玻璃化温度又升高。氯化聚乙烯有两种典型结构，其一是氯原子在大分子链上无规而均匀分布，成为饱和弹性体，其二是氯原子在大分子链上无规则不均匀的嵌段分布，表现出硬塑料的行为。含氯量25％-45％的氯化聚乙烯是一种耐热、耐候及耐燃的特种橡胶。含氯量超过45％的氯化聚乙烯是白色均匀颗粒状无定形固体。由于大分子结构饱和及氯原于的引入，使CPE具有良好的柔韧性、耐臭氧性、耐候性、耐热老化性、耐油性、阻燃性、电性能、耐化学药品性。弹性和耐寒性稍差。
氯化聚乙烯产品分两大类，一类是树脂型，冠以“CPE”标识，另一类是橡胶型，冠以“CM”标识。表征氯化聚乙烯的性能参数有含氯量(用两位数字表示)、残留结晶度(用等级数字或英文字母表示)、原料氯乙烯类型或产品加工流动性也用数字级别或英文字母表。
用于改善胶粘剂的韧性和阻燃性。贮存于阴凉、通风、干燥的库房内。
氯化聚乙烯产品分两大类，一类是树脂型，冠以“CPE”标识，另一类是橡胶型，冠以“CM”标识。表征氯化聚乙烯的性能参数有含氯量(用两位数字表示)、残留结晶度(用等级数字或英文字母表示)、原料氯乙烯类型或产品加工流动性也用数字级别或英文字母表。
用于改善胶粘剂的韧性和阻燃性。贮存于阴凉、通风、干燥的库房内。