1) resistivity minimum
电阻极小
1.
In order to clarify the physical mechanism of the low-temperature resistivity minimum observed in polycrystal and epitaxy films of manganites,the single crystal La2/3Sr1/3MnO3 were studied,which were fabricated in Ar atmosphere by optical-floating-zone method.
为了阐明在锰氧化物多晶以及外延薄膜中存在的低温电阻极小值现象,对La2/3Sr1/3MnO3单晶样品的性质进行研究。
2) Resistivity minima
电阻极小值现象
3) minimum electrical resistivity phenomenon at low temperature
低温电阻率极小
1.
Intrinsic abnormal minimum electrical resistivity phenomenon at low temperature was observed in Perovskite like La 1/3 Nd 1/3 Ba 1/3 MnO 3 and La 1/3 Nd 1/3 Sr 1/3 MnO 3 Oxides with CMR effect.
发现在La1/ 3 Nd1/ 3 Ba1/ 3 MnO3 和La1/ 3 Nd1/ 3 Sr1/ 3 MnO3 材料中存在低温电阻率极小值现象·经曲线拟合分析后 ,认为其机理在于材料中存在类似于磁性杂质对传导电子自旋散射造成的近藤效应 (KondoEffect) ,是出现局域磁有序的结
4) drag minimization
阻力极小
6) polarization resistance
极化电阻
1.
Measurements of corrosion potential and the polarization resistance were used to investigate the electrochemical behavior of HSn70-1AB and BFe30-1-1copper alloys in medium containing sulfate reducing bacteria.
结果表明,铜合金表面生物腐蚀与SRB的生长特性密切相关,SRB处于指数生长期时,HSn70-1AB和BFe30-1-1铜合金的自腐蚀电位(Ecorr)和极化电阻(Rp)均迅速下降,腐蚀加剧,且后者腐蚀速度大于前者;而当SRB进入稳定生长阶段,两种合金的Ecorr和Rp均缓慢下降,腐蚀速度减缓,且二者腐蚀速度接近。
2.
Composite cathode could improve the performance and efficiency of the solid oxide fuel cell at high temperature,decrease the over-potential,polarization resistance and interfacial resistance.
复合阴极可以提高固体氧化物燃料电池(SOFC)在高温下的性能和效率,降低过电位、极化电阻和界面电阻。
3.
The codeposition of nickel—phosphorus alloys in phosphorous acid system as well as their corrosion resistance in neutral sodium chloride solutions were investigated using various techniques such as electrodepositing at constant current, corrosion potential and polarization resistance, XRD, SEM and XPS.
用恒电流沉积、腐蚀电位和极化电阻等方法研究了 H3PO3体系中 Ni-P合金的电沉积及其镀层的耐蚀性能 ,用 XRD、 XPS、 SEM检测了镀层的晶形、组成和表面形貌 ,探讨了沉积条件对镀层耐蚀性能的影响 。
补充资料：极小值
极小值
nunnnum
赫母票惠东谭巍瓢黑黑:n刀n刀刀uln points).