1) carbon reducing reaction
碳还原反应
1.
Mechanism of carbon reducing reaction in preparing strontium carbonate by carbon reducing method was studied.
研究了碳还原法制备碳酸锶过程中碳还原反应的机理。
2) Carbothermal reduction
碳热还原反应
1.
Mechanism and thermodynamics of carbothermal reduction of alumina;
氧化铝碳热还原反应机制及其热力学
2.
Ultrafine SiC powder was synthesized by carbothermal reduction of the precursor of carbon black coated with water glass, which was prepared by spray drying the slurry of carbon black and water glass.
以水玻璃和炭黑为原料,采用喷雾干燥技术制备水玻璃包覆炭黑前驱粉体,经碳热还原反应合成SiC。
3.
The mechanism of mechanical activation synthesis has been investigated in the carbothermal reduction of alumina.
用两种球磨方式活化氧化铝 ,用化学分析法测量氧化铝碳热还原反应后生成氮化铝的转化率 ,考察了球磨活化对氧化铝碳热还原反应合成氮化铝的作用 ,研究了机械力活化合成的机制。
3) carbothermal reduction nitridation
碳热还原反应
1.
The effects of high-energy ball milling including the fining and mechanochemical on the carbothermal reduction nitridation of alumina were investigated.
研究了高能球磨氧化铝的细化和机械力化学作用及球磨对碳热还原反应合成氮化铝 (AlN)的影响。
2.
The carbothermal reduction nitridation reaction was promoted greatly after the milling of alumina for 20 hours.
研究了氧化铝球磨对碳热还原反应合成氮化铝的作用。
3.
Several mechanisms of AlN synthesis by carbothermal reduction nitridation method were reviewed.
本文综述了碳热还原反应制备ＡｌＮ的各种反应机制，并进行了评述，详述了气－固反应机制和固－固反应机制的特点、实验证据及存在的不足。
4) carbothermic (reaction) reaction
碳热还原反应<冶>
5) carbothermal reduction reaction
碳热还原反应
1.
Then,the SiC-ZrO2 composite was synthesized via a carbothermal reduction reaction at 1 530 ℃ for 4 h in argon atmosphere,with zircon and carbon black as starting materials and La2O3 reagent as additive.
根据有关热力学数据绘制出1 530℃时Si-C-O体系优势区图,在此基础上,以锆英石和碳黑为原料,以化学试剂La2O3为添加剂,在Ar气氛下于1 530℃恒温4 h经碳热还原反应合成出SiC-ZrO2复合材料。
6) Carbothermal reduction nitridation
碳热还原氮化反应
补充资料：碳热还原
carbothermicreduction：用碳作为还原剂和发热剂来冶炼金属称为碳热还原。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。