3) nano TiO 2/silicone acrylic emulsion
硅丙复合乳液
1.
Then it is compounded, through in-situ polymerization, with silicone modified acrylic polymer to prepare a stable nano TiO 2/silicone acrylic emulsion.
采用硅烷偶联剂对纳米TiO2 进行表面处理 ,使其亲水性表面改为亲油性 ,并在其表面接枝上可反应的有机官能团 ,然后通过原位聚合法与有机硅改性丙烯酸聚合物复合 ,制得性能稳定的纳米TiO2 /硅丙复合乳液。
4) styrene-acrylate emulsion
苯丙乳液
1.
Surface modification and characterization of nanometer TiO_2 for nanometer styrene-acrylate emulsion polymerization;
用于合成纳米苯丙乳液的纳米TiO_2表面改性及表征(英文)
2.
Study on synthesis of core-shell type of styrene-acrylate emulsion with silicon;
核/壳型含硅苯丙乳液的合成与研究
3.
Research on Synthesis and Properties of Styrene-acrylate Emulsion in Textile;
纺织用苯丙乳液的合成及性能研究
5) styrene-acrylic emulsion
苯丙乳液
1.
Influence of functional monomer on styrene-acrylic emulsion performance;
功能单体对苯丙乳液性能的影响
2.
Study of styrene-acrylic emulsion modified by double-bond tetra-coordinated silicon;
含四配位硅的烯类单体改性苯丙乳液的研究
6) styrene/acrylic emulsion
苯丙乳液
1.
Vinyltrimethoxysilane was used in polymerization of styrene/acrylic emulsion,the property of emulsion was measured.
用乙烯基三甲氧基硅烷与苯乙烯、丙烯酸酯共聚合成苯丙乳液,对乳液性能进行了检测,并用傅里叶红外光谱对乳液化学结构进行了表征,证明乙烯基三甲氧基硅烷参与了共聚物的合成。
2.
By means of orthogonal testing and overall merit assessment,the influence of polymerization process of the multiple styrene/acrylic emulsion system,monomers for copoly meri.
以苯乙烯和丙烯酸丁酯作为主要单体,甲基丙烯酸及甲基丙烯酸甲酯作为必要成分,采用过硫酸盐作引发剂,在乳化剂作用下进行聚合制得苯丙乳液。
3.
Styrene(ST) as hard monomer, butyl acrylate(BA) as soft monomer, A and B as functional monomers, styrene/acrylic emulsion was synthesized by semicontinuous emulsion polymerization.
以苯乙烯为硬单体,丙烯酸丁酯为软单体,单体A和单体B为功能性单体,采用半连续乳液聚合法合成苯丙乳液,对乳液合成条件进行了研究,对乳液和浸渍后汽车工业滤纸性能进行了检测、分析。
补充资料：苯丙乳液
苯丙乳液是由苯乙烯和丙烯酸酯单体经乳液共聚而得。乳白色液体，带蓝光。固体含量40～45％，粘度80～1500mPa·s，单体残留量0.5%，PH值8～9。苯丙乳液附着力好，胶膜透明，耐水、耐油、耐热、耐老化性能良好。
苯丙乳液用作纸品胶粘剂，也可与淀粉、聚乙烯醇、羧甲基纤维素钠等胶粘剂配合使用。贮存于5～30 ℃的库房内，贮存期1年。
苯丙乳液用作纸品胶粘剂，也可与淀粉、聚乙烯醇、羧甲基纤维素钠等胶粘剂配合使用。贮存于5～30 ℃的库房内，贮存期1年。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。