2) trivalent chromium electroplating
三价铬电镀
1.
A process for trivalent chromium electroplating in sulphate system was established.
开发了一种硫酸盐体系三价铬电镀铬工艺,确定了其所使用的阳极,并将所获得的产品相关性能参数与国外同类产品进行了对比。
2.
At present, trivalent chromium electroplating process has became one of the mostimportant techniques to taking place of the seriously pollutional hexvalent chromiumelectroplating process.
目前，三价铬电镀工艺已经成为取代重污染六价铬电镀的最重要技术之一。
3) trivalent chromium plating
三价铬电镀
1.
Electrochemical behavior of oxide-coated Ti electrode for trivalent chromium plating;
三价铬电镀用氧化物涂层钛电极的电化学行为
2.
In this paper, three types of bath for trivalent chromium plating are gained: chloride-glycine bath, chloride-U bath and sulfate-oxalic bath.
本文研究得到的三种三价铬电镀体系:氯化物-氨基乙酸体系、氯化物-U体系及硫酸盐-草酸体系。
3.
A new trivalent chromium plating process using formate-carboxylic acid salt as complexing agents is studied in this paper.
本文新近研究了一种以甲酸盐-羧酸盐作为络合剂的三价铬电镀新工艺,并对该溶液和镀层进行了性能测试。
4) black trivalent chromium electro-plating
三价黑铬电镀
6) trivalent chromium sulfate plating
三价铬镀铬
1.
The influence of impurity of Cu2+, Zn2+, Ni2+and Fe2+ (content of 50 mg/kg) on deposit’s appearance, thickness and bath’s polarization was discussed in process of trivalent chromium sulfate plating.
研究了硫酸盐三价铬镀铬工艺中铜、锌、铁、镍离子(含量均为50mg/kg)对镀层外观和厚度、镀液极化的影响,比较了不同除杂方法的除杂效果。
补充资料：电镀铬
分子式：
CAS号：
性质：是最重要的防护装饰性镀层之一。这种铬镀层的厚度一般为0.25～2μm，铬镀层在空气中很稳定，反光性能好，并能长期保持其光泽。铬镀层的硬度很高，耐磨耐热性好，因而也常用于机械零件的修复或电镀易磨损件。在此情况下，铬镀层很厚，习惯上称作镀硬铬。其厚度一般为30～80μm，最高达1mm。镀铬溶液的主要成分是铬酸，但还必须有少量阴离子(如SO42-)。为了减少六价铬的污染，有的工厂已采用低浓度的铬酸镀液。
CAS号：
性质：是最重要的防护装饰性镀层之一。这种铬镀层的厚度一般为0.25～2μm，铬镀层在空气中很稳定，反光性能好，并能长期保持其光泽。铬镀层的硬度很高，耐磨耐热性好，因而也常用于机械零件的修复或电镀易磨损件。在此情况下，铬镀层很厚，习惯上称作镀硬铬。其厚度一般为30～80μm，最高达1mm。镀铬溶液的主要成分是铬酸，但还必须有少量阴离子(如SO42-)。为了减少六价铬的污染，有的工厂已采用低浓度的铬酸镀液。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。