1) ultrafine Mo powder
超细钼粉
1.
A novel method for preparation of ultrafine Mo powder was developed,by rapid and homogeneous precipitation.
以浓硝酸酸沉一定浓度的仲钼酸铵溶液,控制反应条件,使其快速均匀沉淀得到胶状的钼酸沉淀,干燥并煅烧后进行氢气还原得到超细钼粉。
2) superfine Mo wire
超细钼丝
1.
8mm Mo wire, and the effect of different annealing treatments on mechanical working properties of superfine Mo wire was researched.
8mm的钼丝在不同退火工艺条件下对超细钼丝加工性能的影响。
3) molybdenum carbide ultra-micron powder
超微碳化钼粉末
4) superfine powder
超细粉体
1.
Application of superfine powder technology in TCM;
超细粉体技术在中药行业中的应用
2.
Rheological behavior of PET blend-modified with TiO_2/ZnO superfine powder
TiO_2/ZnO超细粉体共混改性PET的流变性能
3.
The sub-micro superfine powder of codonopsis pilosula(Franch) Nannf are produced by pulverizer of turbulence,and several elements affecting the diameters of superfine powder are researched at the same time,such as the speed of impeller,the quality of reinforced material and the working time.
利用湍流超细粉碎机制取了党参的亚微米级超细粉体,研究了叶轮转速、加料质量、粉碎时间对粉体粒径的影响,对党参的超细粉碎工艺参数进行了优化;分析了造成粉体团聚的原因,结果表明,叶轮转速的提高是引起粉体团聚的主要因素。
5) ultrafine powder
超细粉体
1.
Preparation of ultrafine powder TiO2 particles by homogeneous precipitation method under boiling reflux conditions;
沸腾回流均相沉淀法合成超细粉体TiO_2
2.
Effect of precipitant on the morphology and performances of ultrafine powder CuO;
沉淀剂对CuO超细粉体形态与性能的影响
3.
Features of Liquid-continuous impinging streams and their Applications in preparation of ultrafine powders;
液体连续相撞击流特性及其在超细粉体制备中的应用
6) micro-pulverized coal
超细煤粉
1.
Dependence of coal compositions on micro-pulverized coal fineness;
超细煤粉粒度对煤质分析特性的影响
2.
Numerical simulation of effect of coal particle size on NO_x reduction in micro-pulverized coal reburning;
煤粉粒度对超细煤粉再燃脱硝效率影响的数值模拟
3.
Study on ignition characteristics of micro-pulverized coal by thermogravimetry;
超细煤粉着火特性的热重分析
补充资料：碳化钼陶瓷
分子式：
CAS号：
性质：钼与碳的化合物为主要成分的陶瓷。主要有两类。(1)以碳化二钼(Mo2C)为主晶相的陶瓷。呈暗灰色。理论密度9.2g/cm3。熔点2690℃。莫氏硬度7。显微硬度1800kg/mm3(负荷50g)。弹性模量22100kg/mm2。热导率6.7×106W/(m·K)。2300℃以上分解。(2)以一碳化一钼(MoC)为主晶相的陶瓷。理论密度8.88g/cm3。熔点2700℃。一般先制成碳化钼粉末(采用钼与碳直接化合法、金属氧化物与碳的还原一化合法、气相沉积法和自蔓延高温合成法)，然后在真空或还原气氛下在碳管炉、钼丝炉、高频真空炉中进行烧结(多采用反应烧结、热压烧结和热等静压烧结)而制成。主要用作超硬工具材料、耐磨材料、发热体材料以及高温结构材料。
CAS号：
性质：钼与碳的化合物为主要成分的陶瓷。主要有两类。(1)以碳化二钼(Mo2C)为主晶相的陶瓷。呈暗灰色。理论密度9.2g/cm3。熔点2690℃。莫氏硬度7。显微硬度1800kg/mm3(负荷50g)。弹性模量22100kg/mm2。热导率6.7×106W/(m·K)。2300℃以上分解。(2)以一碳化一钼(MoC)为主晶相的陶瓷。理论密度8.88g/cm3。熔点2700℃。一般先制成碳化钼粉末(采用钼与碳直接化合法、金属氧化物与碳的还原一化合法、气相沉积法和自蔓延高温合成法)，然后在真空或还原气氛下在碳管炉、钼丝炉、高频真空炉中进行烧结(多采用反应烧结、热压烧结和热等静压烧结)而制成。主要用作超硬工具材料、耐磨材料、发热体材料以及高温结构材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。