2) Nb-Si based alloy
Nb-Si系合金
3) Nb-Ti-Si base multielement alloy
Nb-Ti-Si基多元合金
4) Nb-Cr based multi-element alloy
Nb-Cr系多元合金
1.
A master alloy ingot of Nb-Cr based multi-element alloy has been prepared by vacuum non-consumable arc-melting, and then vacuum consumable arc-melting and heat treated at 1450 ℃ for 24 h and 1000 ℃ for 24 h, then oxidized at 950 ℃ in air for different times for the heat treated samples.
采用真空非自耗+真空自耗电弧熔炼的方法制备了Nb-Cr系多元合金的母合金锭;对母合金进行了1450℃,24h+1000℃,24h的热处理;采用三点弯曲方法测试了合金的室温断裂韧性;进行了950℃不同时间的氧化实验。
2.
The composition of an Nb-Cr based multi-element alloy was designed.
对比分析了电弧熔炼态和不同工艺热处理后的组织特征,研究了热处理温度对Nb-Cr系多元合金组织的影响规律。
6) Nb-Ti-Si ternary system
Nb-Ti-Si三元系
1.
Phase equilibria in the Nb-Ti-Si ternary system at 1 473 K was investigated using diffusion triple technique and electron microprobe analysis (EMPA).
运用扩散偶技术结合电子探针微区成分分析方法对Nb-Ti-Si三元扩散偶进行相分析,测得Nb-Ti-Si三元系1473K下所生成的7个扩散层,分别是TiSi2,TiSi,Ti5Si4,Ti5Si3,Nb5Si3,NbSi2和M3Si,此扩散偶中未发现三元化合物。
补充资料:[3-(aminosulfonyl)-4-chloro-N-(2.3-dihydro-2-methyl-1H-indol-1-yl)benzamide]
分子式:C16H16ClN3O3S
分子量:365.5
CAS号:26807-65-8
性质:暂无
制备方法:暂无
用途:用于轻、中度原发性高血压。
分子量:365.5
CAS号:26807-65-8
性质:暂无
制备方法:暂无
用途:用于轻、中度原发性高血压。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条