1) vacuum destressing annealing
真空去应力
1.
The welding stress,the mechanical property and microstructure of TC4 material electron beam welding sample before and after vacuum destressing annealing were analyed,the best destressing annealing standard was finally determined.
通过对TC4钛合金焊接试件在真空去应力退火前后的焊接应力、力学性能和显微组织进行对比试验分析,最终确定了最佳去应力退火规范。
2) loss of vacuum
失去真空
3) Re-stress
去内应力
4) stress removing after welding
去应力
1.
The paper introduces the design of a new type load-bearing beeam- #" shape in a state important project, stress removing after welding and mechanics tests are also presents herein.
本文介绍了国家某重点工程中一种新型“井”字形承力梁的设计、焊后去应力处理和力学试验。
5) three dimensional stress simulation analysis
空间应力仿真分析
6) vacuum induction
真空感应
1.
Technical research on 921A and HZS60B welding wires by vacuum induction melting;
真空感应熔炼921A焊丝和HZS60B焊芯钢丝的工艺研究
2.
Automatic control of vacuum induction CVI/CVD system;
真空感应CVI/CVD系统自动化控制技术
3.
The structure and function of vacuum induction CVI/CVD system is presented.
介绍了真空感应CVI/CVD系统结构、功能。
补充资料：注塑产品内应力
注塑制品的内应力包括两种:一种是注塑制品成型应力,另一种是温度应力
影响内应力的工艺因素
对取向应力的影响在速冷条件下，取向会导致聚合物内应力的形成。
熔体温度高，粘度低，取向度降低，另一方面，由于熔体温度高会使应力松弛加快，促使解取向能力加强。
延长保压时间会导致取向压力增加。
提高注射压力，保压压力，会增大取向压力。
令材料变脆的几种状况。
影响内应力的工艺因素
对取向应力的影响在速冷条件下，取向会导致聚合物内应力的形成。
熔体温度高，粘度低，取向度降低，另一方面，由于熔体温度高会使应力松弛加快，促使解取向能力加强。
延长保压时间会导致取向压力增加。
提高注射压力，保压压力，会增大取向压力。
令材料变脆的几种状况。