1) iron–nickel alloy coating
铁镍合金镀层
2) Ni-Fe alloy
镍铁合金镀层
1.
Microstructure and thermal stability of nanocrystalline Ni-Fe alloy coatings synthesized by brush plating;
电刷镀镍铁合金镀层的纳米晶结构及其热稳定性
3) Fe-Co-Ni alloy coating
铁-钴-镍合金镀层
1.
In order to solve the repairing problem of worn sliding plate of airplane gun,the technology of brush plating for the Fe-Co-Ni alloy coating on the surface of high strength steel 18Cr2Ni4WA has been researched.
为了解决航炮磨损失效滑板的修复问题,研究了在18Cr2Ni4WA高强度钢表面刷镀铁-钴-镍合金镀层的工艺。
4) Fe-Ni-Cr alloys
铁-镍-铬三元合金镀层
1.
A spectriphotometric determination of the chromium content in Fe-Ni-Cr alloys has been developed by using Cr-DPC system.
本文研究了二苯羰酰二肼(DPC)光度法测定铁-镍-铬三元合金镀层中铬含量的方法。
5) nickel alloy plating
镍合金镀层
1.
However the amount of cobalt sulfate is over 5 g/L,the crystalline of nickel alloy plating .
研究了低含量的钴对镍合金镀层结构和性能的影响,通过扫描电镜观察了镀层形貌、X射线衍射仪测量了镀层内应力,并用电化学极化曲线和腐蚀失重方法分析了镀层的耐蚀性。
6) zinc-iron alloy electroplating bath
镍-铁合金镀液
补充资料：铁镍合金
一种在弱磁场中具有高磁导率和低矫顽力的低频软磁材料。早期铁镍合金用于电话通信，其后采用一种热处理工艺和真空冶炼的方法使合金特性得到较大的提高。含Ni78％的铁镍合金在弱磁场中的磁导率比硅钢高约10～20倍，普遍用于灵敏继电器、磁屏蔽、电话和无线电变压器、精密的交流和直流仪表、电流互感器（见互感器）中。在铁镍合金中加入钼、锰、钴、铜、铬等元素，可得具有更大初始磁导率μi和最大磁导率μm的三元、四元铁镍合金。
铁镍合金具有窄而陡的磁滞回线，在弱磁场中具有很大磁导率和很小的矫顽力,但它的电阻率不大,只适合在1 兆赫以下的频率范围工作，否则涡流损耗太大。铁镍合金的加工性能好，可制成各种形状复杂、尺寸要求精确的元件。但它的磁性能对机械应力比较敏感，工艺因素对磁性能的影响较大，如冲压会使μb下降，因而产品性能一致性不易满足。铁镍合金的成本高。常用的铁镍合金的特性和用途列于表。
铁镍合金具有窄而陡的磁滞回线，在弱磁场中具有很大磁导率和很小的矫顽力,但它的电阻率不大,只适合在1 兆赫以下的频率范围工作，否则涡流损耗太大。铁镍合金的加工性能好，可制成各种形状复杂、尺寸要求精确的元件。但它的磁性能对机械应力比较敏感，工艺因素对磁性能的影响较大，如冲压会使μb下降，因而产品性能一致性不易满足。铁镍合金的成本高。常用的铁镍合金的特性和用途列于表。