1) cryptomelane-type hydrous manganese dioxide
隐钾锰型水合二氧化锰
1.
Synthesis of cryptomelane-type hydrous manganese dioxide and its ion exchange thermodynamics for K~+
以硫酸锰和高锰酸钾为原料合成隐钾锰型水合二氧化锰(CRYMO),酸改型后得晶体结构为α-MnO2的钾离子筛(CRYMO-H)。
2) rubidium doped cryptomelante-type manganese dioxide
隐铷锰型水合二氧化锰
3) CRYMO
隐钾锰型水合MnO2
4) birnessite manganese oxide
水钠锰矿型锰氧化合物
1.
The result indicated that the nanocomposite had improved charge-discharge recycleability better than birnessite manganese oxide.
将水钠锰矿型锰氧化合物沉淀于剥离状态的氧化石墨层上,利用被锰氧化合物单层所 包裹的氧化石墨的自配列,合成了一种新型氧化石墨-锰氧化合物隔层排列的纳米复合材料。
5) Hydrated manganese dioxide
水合二氧化锰
1.
In this paper,two ways for cycling use of hydrated manganese dioxide formed in the coprecipitation process are developed.
共沉淀法所得大量水合二氧化锰可用水洗碱煮,烘干后直接循环使用。
2.
Lab-scale coagulation experiments on the treatment of simulated raw water were carried out using hydrated manganese dioxide produced by potassium permanganate and sodium sulfite composite.
采用高锰酸钾与亚硫酸钠复合还原剂制备水合二氧化锰并用其处理人工配水,考察了该水合二氧化锰的混凝效能、影响因素及可能的除浊机制。
6) Hydrous manganese oxide
水合氧化锰
补充资料：醋酸锰
分子式：C4H6MnO4·4H2O
分子量：245.09
CAS号：6156-78-1
性质：淡红色透明单斜晶体。熔点为80℃；相对密度1.589。溶于水及醇。
制备方法：由锰与乙酸反应制得。先用5%的消酸将金属锰浸泡5min，再用蒸馏水漂洗数次，洗至pH值为8。然后，加入乙酸进行合成反应，先制得乙酸锰粗品，再加少量活性炭，以除去其中的铁、铅等金属离子。然后过滤，滤液用乙酸（化学纯）调节pH至3-4后，蒸发至相对密度为1.30，再冷却、结晶、离心分离、干燥（50℃以下），即得成品。原料消耗（kg/t）工酸（工业品） 1100金属锰（工业品） 380硝酸（工业品） 10
用途：该品是聚酯树脂的原料—二甲苯高温氧化的催化剂。还可用作染色媒染剂，涂料、清漆的干燥剂，以及氧化过程的催化剂等。
分子量：245.09
CAS号：6156-78-1
性质：淡红色透明单斜晶体。熔点为80℃；相对密度1.589。溶于水及醇。
制备方法：由锰与乙酸反应制得。先用5%的消酸将金属锰浸泡5min，再用蒸馏水漂洗数次，洗至pH值为8。然后，加入乙酸进行合成反应，先制得乙酸锰粗品，再加少量活性炭，以除去其中的铁、铅等金属离子。然后过滤，滤液用乙酸（化学纯）调节pH至3-4后，蒸发至相对密度为1.30，再冷却、结晶、离心分离、干燥（50℃以下），即得成品。原料消耗（kg/t）工酸（工业品） 1100金属锰（工业品） 380硝酸（工业品） 10
用途：该品是聚酯树脂的原料—二甲苯高温氧化的催化剂。还可用作染色媒染剂，涂料、清漆的干燥剂，以及氧化过程的催化剂等。