1) bainitic welding rod
贝氏体焊条
1.
In order to solve the traditional bainitic welding rod build-up welding rail when preheating before welding and heat treatment after welding, U71Mn rail was directly welding repaired using bainitic welding rod.
为了解决传统焊条在堆焊铁路钢轨时焊前必须预热、焊后进行热处理等不足,本文采用自制的贝氏体焊条对U71Mn钢轨进行直接堆焊修复,分析研究了在不同的电流下直接堆焊钢轨其组织、性能的变化。
2) bainite ferrite
板条贝氏体
1.
It is shown that there are different microstructures under two kinds of cooling rate of as rolled steel,and bainite ferrite microstructure obtained by accelerated cooling has higher strength than granular bainite microstructure after.
结果显示,钢轧后,在两种冷速下得到的组织形貌差别较大,快速水冷得到强度较高的板条贝氏体组织,缓冷得到强度较低的粒状贝氏体组织,粒状贝氏体的形成温度较高,没有明显板条特征;板条贝氏体屈服强度比粒状贝氏体高出278MPa,抗拉强度高出307MPa;而粒状贝氏体的塑性和韧性指标明显优于板条贝氏体,延伸率和-20℃低温冲击功指标是板条贝氏体的近3倍。
2.
Mechanical properties of phase transformation microstructure of ULCB steel,including granular bainite and bainite ferrite have been contrasted.
对ULCB钢的主要相变组织粒状贝氏体与板条贝氏体进行了力学性能比较,结果显示粒状贝氏体与板条贝氏体是完全不同的两种组织,较高温度相变产物粒状贝氏体组织较为粗大,对强度和韧性有不利影响,而较低温度相变产物板条贝氏体组织对强度和韧性是有益的。
3) bainitic lath
贝氏体板条
5) sheaf of bainitic lath
贝氏体板条束
6) stripe granular bainite
条形粒状贝氏体
1.
A temper structure of stripe granular bainites was given out through a lot of tests and studies,which can be used in barrel and be highly imporoved the life of barrel.
研究了轻武器身管钢在不同热处理条件下（调质态和高温正火加回火态）的显微组织与力学性能，提出了条形粒状贝氏体回火组织可使身管寿命大幅度提高。
补充资料：贝氏体
分子式：
CAS号：
性质：又称贝茵体。钢中相形态之一。钢过冷奥氏体的中温(350～550℃)转变产物，α-Fe和Fe3C的复相组织。贝氏体转变温度介于珠光体转变与马氏体转变之间。在贝氏体转变温度偏高区域转变产物叫上贝氏体(up bai-nite)，其外观形貌似羽毛状，也称羽毛状贝氏体。冲击韧性较差，生产上应力求避免。在贝氏体转变温度下端偏低温度区域转变产物叫下贝氏体。其冲击韧性较好。为提高韧性，生产上应通过热处理控制获得下贝氏体。
CAS号：
性质：又称贝茵体。钢中相形态之一。钢过冷奥氏体的中温(350～550℃)转变产物，α-Fe和Fe3C的复相组织。贝氏体转变温度介于珠光体转变与马氏体转变之间。在贝氏体转变温度偏高区域转变产物叫上贝氏体(up bai-nite)，其外观形貌似羽毛状，也称羽毛状贝氏体。冲击韧性较差，生产上应力求避免。在贝氏体转变温度下端偏低温度区域转变产物叫下贝氏体。其冲击韧性较好。为提高韧性，生产上应通过热处理控制获得下贝氏体。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。