1) high-temperature brittle zone
高温脆性区
1.
The solidification structure has a great impact on solidification cracks which mainly occurred in the high-temperature brittle zone in the continuous casting process.
结合相图并利用示差扫描量热仪(DSC)、定向凝固实验系统和Gleeble-3800热模拟实验机,在对1Cr18Ni9Ti奥氏体不锈钢的熔化和近平衡凝固过程进行分析的基础上,研究了冷却速率对奥氏体不锈钢高温脆性区凝固组织的影响。
2) embrittling temperature range
脆性温区
1.
The forming of embrittling temperature range is conceined with solidified structure and embrittling grain boundary.
结果表明,连铸坯存在1200℃～T_M(熔点)及700～1000℃两个脆性温区,脆性温区的产生与凝固组织及晶界脆化有关。
4) low ductility region
脆性温度区
1.
It is found that the low ductility region Ⅲ is between 920 and 730 ℃.
为了研究残余元素Cu、As和Sn对钢高温延塑性的影响,采用Gleeble-1500热模拟试验机测试了含有一定量Cu、As和Sn低合金钢连铸坯的高温延塑性,得到了低合金钢第Ⅲ脆性温度区在920～730℃之间。
2.
It was found that the low ductility temperature regionⅠof low alloy steel was between ts and 1340 ℃ and the low ductility region Ⅲ was between 920-730 ℃.
低合金钢的第Ⅰ脆性温度区在ts~1 340℃之间,第Ⅲ脆性温度区在920~730℃之间。
5) temperature zone of fragility
脆性温度区间
6) BTR(brittle temperature range)
[冶]脆性温度区