1) aligned TiO2 nanotube thin film
TiO2纳米管阵列薄膜
1.
The aligned TiO2 nanotube thin films were fabricated on the Ti substrate in 0.
0mol/L NH4H2PO4的混合溶液中,利用阳极氧化的方法在钛基体上原位合成自组装有序的TiO2纳米管阵列薄膜材料,研究不同热处理温度对薄膜晶型及光生阴极保护能力的影响。
2) TiO2 nanotube arrays membranes
TiO2纳米管阵列膜
3) nanotube array film
纳米管阵列薄膜
1.
Thermal stability of TiO_2 nanotube array films;
TiO_2纳米管阵列薄膜的热稳定性
2.
High density and uniform titanium dioxide nanotube array films on Al plate were successfully prepared via liquid phase deposition method by immersing the anodic aluminum oxide (AAO) templates on aluminum substrate in ammonium hexafluorotitanate aqueous solution.
采用液相沉积法,将铝基多孔阳极氧化铝(AAO)模板浸入到(NH4)2TiF6溶液中,制备出高度有序的TiO2纳米管阵列薄膜,并在不同的温度下进行了热处理。
4) TiO 2 nanowires array film
TiO2纳米线阵列膜
5) TiO2 nanotube arrays
TiO2纳米管阵列
1.
The research progress of TiO2 nanotube arrays prepared by anodic oxidation under static voltage,including doped TiO2 nanotubes and application research of TiO2 nanotube arrays were reviewed in this paper.
综述了恒压阳极氧化法制备TiO2纳米管阵列的研究进展;系统归纳了纳米管阵列在制备、改性、应用方面的研究进展,并对TiO2纳米管阵列的应用研究提出了新的展望。
2.
Self-organized TiO2 nanotube arrays with micro-scale length were prepared on fluorine-doped tin oxide (FTO) conducting glass in NH4F/glycerol electrolyte by electrochemical anodization of pure titanium films deposited by radio frequency magnetron sputtering (RFMS) at room temperature.
在掺氟的SnO2(FTO)导电玻璃衬底上采用射频磁控溅射的方法室温沉积纯Ti薄膜,以NH4F/甘油为电解液,经电化学阳极氧化得到结构有序、微米级的TiO2纳米管阵列/FTO复合结构,并通过场发射扫描电子显微镜(FESEM)、X射线衍射(XRD)以及光电化学的方法对纳米管阵列进行了表征。
3.
The Fe-doped TiO2 nanotube arrays were fabricated in Fe(NO3)3-HF mixing solutions by electrochemical anodic oxidation method,and characterized by FESEM,Raman,XPS and DRS.
应用电化学阳极氧化法,以Fe(NO3)3-HF的混合水溶液作电解液在Ti基底上制备Fe掺杂TiO2纳米管阵列。
6) TiO2 nanotube array
TiO2纳米管阵列
1.
TiO2 nanotube array material was prepared by anodic oxidation of a pure titanium sheet.
在400℃下煅烧2h后,TiO2纳米管阵列为锐钛矿型,并且结构保持良好,没有出现变形、剥落的现象。
2.
TiO2 nanotube arrays were prepared by the electrochemical anodization on pure Ti surfaces,and their photoelectrochemical activity was examined.
应用电化学阳极氧化法在纯Ti基底上制备高度有序的TiO2纳米管阵列,考察了Ti/TiO2光阳极的光电化学响应。
补充资料：Tio2
钛的氧化物——二氧化钛，是雪白的粉末，是最好的白色颜料，俗称钛白。以前，人们开采钛矿，主要目的便是为了获得二氧化钛。钛白的粘附力强，不易起化学变化，永远是雪白的。特别可贵的是钛白无毒。它的熔点很高，被用来制造耐火玻璃，釉料，珐琅、陶土、耐高温的实验器皿等。
二氧化钛是世界上最白的东西， l克二氧化钛可以把 450多平方厘米的面积涂得雪白。它比常用的白颜料一—锌钡白还要白5倍，因此是调制白油漆的最好颜料。世界上用作颜料的二氧化钛，一年多到几十万吨。二氧化钛可以加在纸里，使纸变白并且不透明，效果比其他物质大10倍，因此，钞票纸和美术品用纸就要加二氧化钛。此外，为了使塑料的颜色变浅，使人造丝光泽柔和，有时也要添加二氧化钛。在橡胶工业上，二氧化钛还被用作为白色橡胶的填料。