1) hydroxyl-terminated poly(L-lactic acid)
端羟基聚L-乳酸
1.
The hydroxyl-terminated poly(L-lactic acid) prepolymer is prepared by the melt direct polycondensation process with polyethylene glycol and L-lactic acid,and isocyanate-terminated nitrile rubber(ITBN) is synthesized with toluene-2,4-di-iso-cyanate(TDI),hydroxyl-terminated nitrile rubber(HTBN).
以聚乙二醇和L-乳酸直接熔融缩聚法制备端羟基聚L-乳酸预聚物(HO-PLLA-OH),以甲苯-2,4-二异氰酸酯(TDI)与端羟基丁腈橡胶(HTBN)进行反应,合成了端异氰酸酯基丁腈橡胶(ITBN),然后再将端羟基聚L-乳酸与端异氰酸酯基丁腈橡胶发生偶联反应,合成了乳酸-丁腈橡胶嵌段共聚物,其分子质量高于原料端羟基聚L-乳酸,分子质量分布也比端羟基聚L-乳酸宽。
2) hydroxyl-terminated PLA
端羟基聚乳酸
1.
The degradation of the HTPB/liquefaction MDI polyurethane modified by hydroxyl-terminated PLA in several different media was studied.
对端羟基聚乳酸(PLA-OH)改性HTPB/液化MDI型聚氨酯在不同介质中的降解进行了研究,采用扫描电镜(SEM)观察。
3) poly(LA-co-(Glc-alt-N~ε-Carbonylbenzoxy-L-Lys))
聚(羟基乙酸-Nε-苄氧羰基-L-赖氨酸-乳酸)
4) poly[LA-co-(GA-alt-Lys)]
聚(乳酸-羟基乙酸-L-赖氨酸)
5) Poly[LA-(Glc-Lys)]
聚(羟基乙酸-L-赖氨酸-乳酸)
6) poly[LA-(Glc-Lys)]/NGF/β-TCP
聚(羟基乙酸-L-赖氨酸-乳酸)/NGF/β-TCP
补充资料：多孔羟基磷灰石陶瓷-聚乳酸复合材料
分子式：
CAS号：
性质：有聚乳酸浸渍涂层的多孔羟基磷灰石(HA)复合材料。将多孔珊瑚状的HA陶瓷浸入DL-聚乳酸的丙酮溶液中(丙酮：聚乳酸=3:1～30:1)，取出干燥8～12h而制得。该复合材料较之未涂层材料，其压缩强度提高近4倍，压缩刚性提高30％，断裂吸收也提高30％左右。动物实验结果表明，这种复合材料已具有类似于来涂层的多孔HA陶瓷的成骨性能，但其初始强度已大大提高。
CAS号：
性质：有聚乳酸浸渍涂层的多孔羟基磷灰石(HA)复合材料。将多孔珊瑚状的HA陶瓷浸入DL-聚乳酸的丙酮溶液中(丙酮：聚乳酸=3:1～30:1)，取出干燥8～12h而制得。该复合材料较之未涂层材料，其压缩强度提高近4倍，压缩刚性提高30％，断裂吸收也提高30％左右。动物实验结果表明，这种复合材料已具有类似于来涂层的多孔HA陶瓷的成骨性能，但其初始强度已大大提高。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。