1) manganese phosphor
锰磷化
1.
In this article is a kind of technological analysis of manganese phosphor under high temperature is introduced.
分析了一种高温锰磷化工艺,讨论槽液各参数的变化对磷化膜品质的影响、槽液的控制管理及磷化膜的检测,总结工艺控制的要点,获得稳定良好的磷化膜。
2) manganese-salt phosphating
锰盐磷化
1.
In order to satisfiedly meet the special quality requirements that the from AIF company,A high-temperature manganese-salt phosphating process was studied.
介绍了一种高温锰盐磷化工艺,讨论了槽液总酸度和游离酸度、铁离子含量、磷化温度等因素对锰盐磷化膜质量的影响情况,总结了生产应用中的工艺控制要点。
4) Phosphorizing Film of Manganese
锰磷化膜
5) Zn-Mn system phosphating
锌锰系磷化
1.
A cleaning Zn-Mn system phosphating solution used in surface pretreatment of iron and steel at room temperature was developed in order to perform cleaning phosphating production at room temperature.
为使磷化实现清洁生产,开发了一种用于钢铁表面涂装前处理的清洁型常温锌锰系磷化液,实现了磷化液的所有分子均能参加成膜反应,且产物为磷化膜、水、沉渣或在磷化膜干燥过程中挥发物的设计思想。
6) manganese phosphate coating
锰系磷化膜
补充资料：材料保护:磷化与铬酸盐化
磷化与铬酸盐化
金属在含有游离磷酸和易溶的硷﹑酸液中﹐利用表面附近的溶液酸硷度的变化获得难溶磷酸盐膜的材料保护技术。这种膜是金属在含有 6价铬和矿物性酸为主要组分的溶液中所形成的非结晶的无孔保护覆层。磷化广泛用於钢铁製品高级涂装层的前处理﹐还可与防锈油脂结合应用﹐延长有效保护期。磷化一般在接近溶液的沸点的温度下进行﹐硷化槽中的沉渣需要经常清理。铬酸盐化广泛用於锌压铸件﹑热浸锌件和镀锌镀鎘件上﹐形成的覆层能防止零件在潮湿环境中生锈﹐并能提高金属件的抗蚀性和改善外观。铝製品上的铬酸盐化有利於涂装﹐也能改善其抗蚀性和外观。
金属在含有游离磷酸和易溶的硷﹑酸液中﹐利用表面附近的溶液酸硷度的变化获得难溶磷酸盐膜的材料保护技术。这种膜是金属在含有 6价铬和矿物性酸为主要组分的溶液中所形成的非结晶的无孔保护覆层。磷化广泛用於钢铁製品高级涂装层的前处理﹐还可与防锈油脂结合应用﹐延长有效保护期。磷化一般在接近溶液的沸点的温度下进行﹐硷化槽中的沉渣需要经常清理。铬酸盐化广泛用於锌压铸件﹑热浸锌件和镀锌镀鎘件上﹐形成的覆层能防止零件在潮湿环境中生锈﹐并能提高金属件的抗蚀性和改善外观。铝製品上的铬酸盐化有利於涂装﹐也能改善其抗蚀性和外观。