1) modified high manganese steel
改性高锰钢
1.
The impact corrosion and abrasion behavior of high manganese steel and modified high manganese steel containing some Lanthanum used as the liner of wet-grinders in acidic-ironstone slurry and at impact energy of 1.
利用改造后的MLD-10型冲击腐蚀试验机,研究了含有一定镧元素的改性高锰钢和高锰钢冶金矿山衬板钢在铁矿石酸性矿浆中的冲击腐蚀磨损行为;采用扫描电子显微镜观察了试样磨损表面形貌,用光学显微镜分析了垂直于试样磨损表面的亚表层金相组织。
2) modification of Rare-earth(RE) high manganese steel
稀土改性高锰钢
1.
To explore the wear mechanism involved in milling processing, modification of Rare-earth(RE) high manganese steel was investigated under the laboratory conditions in this study.
本文针对这种情况，在前人开发的基础上熔炼出湿式磨机衬板用稀土改性高锰钢后，对其冲击腐蚀磨损机理进行了一定的探讨。
3) high-performances Manganese steel
高性能锰钢
4) high-manganese steel
高锰钢
1.
Superficial view of machining features of ZGMn13 high-manganese steel;
浅谈ZGMn13高锰钢的切削加工性
2.
This paper presents related technical matters about high-manganese steel frogs'deposit welding,in- cluding the characteristics of various deposit welding techniques,mechanical properties,weldability and defects of high-manganese steel frogs,deposit welding technology,the choice of welding machines and welding rods and its application in production.
介绍了高锰钢辙叉堆焊的有关技术问题,包括各种堆焊技术的特点,高锰钢的力学性能,高锰钢辙叉的焊接性及缺陷、堆焊工艺及焊机焊条的选择以及在生产中的应用。
3.
The high chrome cast-iron added a variety of drib and microscale elements was used to make the flat hammer in overpressure turbine crusher,which can improve the wearing resistance and synthesize mechanical property of the products greatly,and the life of the products is 4 times longer than the former high-manganese steel.
在高铬铸铁中加入多种少量和微量合金元素用以生产反击式破碎机板锤,可使产品耐磨性和综合力学性能得到很大程度的改善,使用寿命比原用高锰钢提高4倍以上。
5) hadfield steel
高锰钢
1.
Using cumulate-welding technology,a layer of WC hard metal was compounded on the matrix surface of hadfield steel,and high wear resistance and high toughness WC/Mn13 composites was successfully fabricated.
采用堆焊工艺在高锰钢的基体表面复合上一层WC硬质合金材料,获得了一种具有高耐磨性和高韧性的复合材料。
2.
The hardness change of cold rolling hadfield steel with different deformation was tested,through the cold rolling deformation of hadfield.
通过对高锰钢进行冷轧变形,考察了不同变形量下冷轧高锰钢的硬度变化,利用自制三体磨料磨损试验机测试了不同磨料磨损工况下,固溶态及其冷轧态的磨损特性。
3.
A nano scale grains surface layer on Hadfield steel was produced by shot peening treat- ment.
利用传统的喷丸技术,在高锰钢表面制备出了具有纳米晶结构特征的表层,并利用X射线衍射仪及高分辨透射电子显微镜表征了表面纳米晶的微观组织结构特征。
6) austenitic manganese steel
高锰钢
1.
Cutting experimental study of new material tools for austenitic manganese steel riding wheel;
煤矿大型高锰钢托轮的新型刀具切削试验研究
2.
The cutting contrast experiments of austenitic manganese steel with compound SiC, compound Si3N4 and TiN coated carbide are researched.
用于露天煤矿大型托轮的高锰钢属于难加工材料。
3.
The cutting experiments of austenitic manganese steel, which serves as large riding wheels at opencut coal mine,were carried out using different cutting tools.
采用新型复合SiC、复合Si3N4和TiN涂层刀具对用于露天煤矿大型拖轮的高锰钢进行了切削加工对比研究,测量了切削温度、后刀面磨损量与切削时间或切削速度的关系曲线,以及刀具前、后刀面显微磨损、破损形貌和化学变化。
补充资料：高锰钢273
Hadfieldsteel：含碳约1、含锰11~14的钢。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。