1) wet-screened mass concrete
湿筛大骨料混凝土
1.
The experimental researches on weight loss,uniaxial compression strength of wet-screened mass concrete after 0,50,100,150,200,250,300 freeze-thaw cycles are carried out.
对经过0、50、100、150、200、250、300次冻融循环作用后的湿筛大骨料混凝土试件进行了质量损失、单轴抗压试验研究。
2) wet-screened aggregate concrete
湿筛混凝土
1.
Experimental study on properties of wet-screened aggregate concrete after freezing and thawing cycles
湿筛混凝土冻融循环后性能的试验研究
3) mass concrete
大骨料混凝土
1.
Study on the Behaviour of Mass Concrete under Complex Stress State with Tests and Numerical Modeling;
复杂应力状态下大骨料混凝土力学特性的试验研究和分析
2.
In order to meet the requirement of the nonlinear analysis and design for the mass concrete structures,the deformation behavior and strength of three-graded concrete specimens 25 cm×25 cm×40 cm with the maximum aggregate size 80 mm and the corresponding wet-screened concrete specimens 15 cm×15 cm×30 cm with the maximum aggregate size 40 mm are studied experimentally.
最后分别在主应力空间和八面体应力空间建立大骨料混凝土的破坏准则,这为水工大体积混凝土按多轴强度理论进行设计提供了试验依据。
4) concrete aggregate
混凝土骨料
1.
Development of concrete aggregate production technology in water and hydropower project construction in China;
我国水利水电工程混凝土骨料生产技术的发展
2.
Regarding the reclamation of dam and the plan of material source for concrete aggregate as emphases, this article discusses the balance and utilizing of excavate material in whole project, in the premise of guaranting construction quality and construction safety, it fully considers construction schedule and construction method, and the excavate material is fully utiliz.
为此,以坝体填筑和混凝土骨料料源规划为重点对全工程的开挖料料物平衡与利用进行了研究,在保证工程质量和安全的前提下,全面考虑施工进度、施工方法,充分利用工程开挖料作为混凝土骨料和坝体填筑料,以达到优化工程布置降低工程造价的目标。
3.
This thesis has put main focus on how to apply excavated spoil to make concrete aggregate to meet the need for spoil disposing technologies.
本论文主要研究如何利用建筑物开挖石渣制备混凝土骨料。
5) lightweight aggregate concrete with big fluidity
大流动性轻骨料混凝土
1.
Adoption of viscous agent is a key technique to ensure lightweight aggregate concrete with big fluidity to have good performances.
增粘剂的采用是保证大流动性轻骨料混凝土具有优良性能的关键。
6) specified density concrete
混合骨料混凝土
1.
Effect of prewetting degree of lightweight aggregate on mechanical properties of specified density concrete;
轻骨料预湿程度对混合骨料混凝土力学性能的影响
补充资料：混凝土骨料
混凝土骨料
concrete aggregate
粗加n率。骨料内部和表面常有一些毛细孔使骨料吸水和含水。骨料的吸水率与母岩的孔隙率有直接关系。因而孔隙率大，影响混凝土的抗冻性、抗磨性和化学稳定性。砂粒吸水后会导致体积膨胀，称为砂的容胀现象，它对混凝土配合比有重大影响。 颗粒形状和表面状态骨料颗粒形状有球形、棱形、片形、针状等。球形多为卵砾石及河沙，棱形为碎石，针片状多见于薄片岩石。球形骨料拌制的混凝土和易性好。碎石骨料表面粗糙与水泥的胶结良好，同样配比的混凝土其强度较卵石混凝土高。针片状颗粒拌制的混凝土和易性差，同时由于其表面积大，水泥用量也高。 级配混凝土中各级骨料粒径颗粒的含量组合比率称为骨料的级配。良好级配的混凝土水泥用量较少，用较少水量能制成和易性好，离析和泌水少的流态混凝土。水工混凝土粗骨料通常按粒径分为4级，其中，“小石”粒径为5~20 mm，“中石”为20一40 mm，“大中”为40一80 mm，“特大石”为80一150 mm(或80~120 mm)。其细度模数多采用6.25一8.30。细骨料一般分为6级，粒径自。.15一smm。细度模数多采用2 .0~3.0。 热性能骨料的热性能主要有比热、导热系数、导温系数和热膨胀系数。它们与混凝土温度裂缝的关系密切，与混凝土抗冻融能力有关。石灰岩的热膨胀系数较低，约为4.4 x 10一“/C，是生产混凝土骨料的好材料。天然卵砾石是一种不均质的混合料，用它拌制的混凝土其热膨胀系数约为5.5只l。’“/C。 有害物质含量有害物质包括猫土、淤泥、软弱颗粒、有机杂质、硫化物、云母及化学盐类等。这些杂质阻碍水泥与骨料胶结，妨碍水泥的正常水化或与水泥中的成分起化学反应，导致混凝土强度和耐久性下降。它们还可能引起需水量加大，减弱馄凝土物理性能。中国《水工混凝土施工规范》(S DJ 207一82)中规定的杂质允许含量见表1和表2。 碱活性骨料反应含有能与水泥中的碱产生化学反应的盐类成分的骨料叫碱活性骨料。碱活性骨料反应有两种:碱一硅酸盐类反应和碱一碳酸盐类反应。 (1)碱一硅酸盐类反应。对于蛋白石、玉髓、鳞石英、方石英、火山玻璃、隐晶质变形石英等活性骨料，水泥中的碱(氧化钠Na20和氧化钾KZ())与骨料中的氧化硅起反应，可生成硅酸钠凝胶。硅酸钠吸水后体积膨胀，初期表现为混凝土表面裂缝上出现透明的凝胶分泌物，后变为白色固体，最后导致混凝土破坏。发生碱一硅酸盐类反应的条件一般为:①水泥的含碱量超过0.6%。②活性骨料含量超过1写。③处于潮湿的环境 中。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。