1) weld toughness
焊缝韧性
1.
Approved by the research consequence,original austenite grain size has significant effect on weld toughness.
针对这种高钢级厚板管线钢埋弧焊接条件下出现的焊缝韧性波动,采用SEM、能谱分析等对焊缝微观组织、冲击断口形貌、成分偏析、焊缝夹杂物、焊丝纯净度等进行了分析。
2.
According to the fact that the fluctuation of weld toughness at low welding speeds,the weld microstructure,appearances of impact fracture,composition segregation,purity of the plate and welding materials were analyzed by adopting light microscope and SEM,etc.
针对低速下焊缝韧性的波动,采用光镜、SEM等对焊缝微观组织变化、冲击断口形貌、成分偏析、板材及焊材纯净度等进行了分析。
3) welded metal toughness
焊缝金属韧性
4) welding joint creeprupture strength
焊接韧性
5) impact toughness of weld metal
焊缝冲击韧度
1.
It was found that impact toughness of weld metal was maximum using carbon arc air gouging, and it was minimum using acid backing.
研究了平对接焊接试板不同的清根方式对CO2气保护药芯焊丝焊缝冲击韧度的影响。
6) weld metal toughness
焊缝金属韧度
补充资料：冲击韧性
分子式：
CAS号：
性质：表征材料抗冲击性的物理量。简支梁和悬臂梁冲击试验中，在冲击负荷作用下试样破坏时吸收的能量与其截面积之比(kJ/m2)。试样可以无缺口或有缺口；有缺口试样可降低破坏时所需之能量，称缺口冲击强度，截面积是缺口底部的截面积。该指标是材料的一项重要性能，有时也称抗冲强度或冲击韧性。另外也还有许多其他的抗冲击的试验方法以测定专指的一些抗冲击性能。例如：落锤冲击、落镖冲击等。冲击强度随升温而增大，尤其是在玻璃化温度附近。结晶时，特别是生成大尺寸的球晶结构往往使冲击强度降低。加入橡胶类聚合物等增韧剂则可提高冲击强度。
CAS号：
性质：表征材料抗冲击性的物理量。简支梁和悬臂梁冲击试验中，在冲击负荷作用下试样破坏时吸收的能量与其截面积之比(kJ/m2)。试样可以无缺口或有缺口；有缺口试样可降低破坏时所需之能量，称缺口冲击强度，截面积是缺口底部的截面积。该指标是材料的一项重要性能，有时也称抗冲强度或冲击韧性。另外也还有许多其他的抗冲击的试验方法以测定专指的一些抗冲击性能。例如：落锤冲击、落镖冲击等。冲击强度随升温而增大，尤其是在玻璃化温度附近。结晶时，特别是生成大尺寸的球晶结构往往使冲击强度降低。加入橡胶类聚合物等增韧剂则可提高冲击强度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。