1) concrete beam reinforced with aramid fiber sheet
芳纶纤维片材加固混凝土梁
1.
Analysis on bending failure of concrete beam reinforced with aramid fiber sheet
芳纶纤维片材加固混凝土梁的弯曲破坏分析
3) aramid fiber reinforced plastics
芳纶纤维片材
1.
Through the shear tests of damaged reinforced concrete (RC) beams with simple supports,the shear-resistant performance of the declining cross section of RC beams reinforced by aramid fiber reinforced plastics (AFRP) was experimentally studied.
通过已损伤的钢筋混凝土简支梁的抗剪试验 ,对用芳纶纤维片材AFRP(AramidFiberReinforcedPlastics)加固钢筋混凝土梁的斜截面抗剪性能进行了试验研究 。
4) hybrid?fiber?sheet strengthened concrete beams
混杂纤维布加固混凝土梁
5) the load-bearing capacity on reinforced concrete beam strengthened with frp
纤维布加固钢筋混凝土梁的承载力
补充资料：芳纶纤维
芳纶纤维的国外商品名为Kavlar纤维，简称K纤维，国产牌号芳纶1414，化学名称为聚对苯二甲酰对苯二胺(p-phenyleneterephthalamide)，相对密度1．43～1．45，无熔融温度，500～570 ℃时分解。芳纶纤维的最大特点是密度低、强度高、耐高温，密度比碳纤维低17％。单丝强度可达3850MPa，比强度约为钢丝的5倍。冲击强度为石墨纤维的6倍。有较高的断裂伸长率，没有碳纤维那样脆。芳纶纤维具有良好的热稳定性、耐火性、耐疲劳性、耐泊性、耐醋碱性。体膨胀系数较小，尺寸稳定性极好。使用温度-190～260 ℃。溶于98％的浓硫酸。
用作树脂高强、耐高温纤维增强填充剂。
用作树脂高强、耐高温纤维增强填充剂。