1) nanosized BaTiO3
纳米BaTiO3
1.
Using nanosized BaTiO3 powders as the raw materials,effects of grain sizes、pH、dispersant、binders、plasticizer contents on the properties of slurry and green tape were investigated,and BaTiO3 sheets were successfully prepared.
以纳米BaTiO3粉体为原料,通过研究BaTiO3的颗粒特性、pH值、分散剂、粘结剂、塑化剂的用量等因素对浆料和流延生坯片性能的影响,成功制备了BaTiO3陶瓷基片。
2) BaTiO3 nanopowder
BaTiO3纳米粉
1.
The advantages of sol-gel and hydrothermal processes were integrated, and sol treatment was introduced to the hydrothermal process enabling perovskite-typed BaTiO3 nanopowders to be synthesized at 搇ow temperatures?conditions through this modified hydrothermal process.
结果表明,采用乙酰丙酮改性的钛酸四丁酯作为Ti源,可有效降低BaTiO3纳米粉的水热合成温度;与常用水热法相比,采用改进的水热法合成BaTiO3纳米粉的温度更低。
3) BaTiO_3 nano-crystal
BaTiO3纳米晶
1.
To analyze Ba,Ti constituents of BaTiO_3 nano-crystal prepared by the sol-gel method,Coordinate titration analysis,precipitation gravimetry and X-ray fluorescence,were introduced to determine the mattev quantity ratio of Ba and Ti.
用配位滴定法、重量法和X-荧光分析法测定了sol-gel法制备的BaTiO3纳米晶中Ba和Ti的物质的量比,结果基本一致,分别为1。
4) nanometer crystal BaTiO3
纳米晶BaTiO3
5) BaTiO3 nanowires
BaTiO3纳米线
6) BaTiO3 powder
BaTiO3纳米粉体
1.
BaTiO3 powder was synthesized by oxalate coprecipitation method,and through the experiment and characterizations of XRD,DTA-TG,IR,TEM the result indicated that the product BaTiO3 was cube,well-proportioned and the size was about 30nm and reunited less.
利用草酸盐共沉淀法合成BaTiO3纳米粉体,通过XRD分析、DTA-TG分析、IR分析及TEM形貌分析等分析手段,对制得的粉体进行了表征和测试,结果表明合成的BaTiO3粉体为单纯的立方相,粒径均匀,颗粒大小在30 nm左右,无严重的团聚现象。