1) poly(butylene succinate-co-terephthalate) (PBST) fabric
聚丁二酸-共-对苯二甲酸丁二醇酯(PBST)织物
1.
A dyeing method of the biodegradable poly(butylene succinate-co-terephthalate) (PBST) fabric with disperse dyes was proposed,and the optimal process conditions were confirmed through experiments:temperature,70 ℃;liquor ratio,1 ∶50;time of treatment,disperse red:40 min,disperse yellow:90 min.
提出了一种分散染料染聚丁二酸-共-对苯二甲酸丁二醇酯(PBST)织物的方法,并确定了染色工艺:温度70℃,浴比1∶50,分散红保温时间40min,分散黄保温时间90min。
2) Poly (butylene succinate-co-terephthalate) (PBST)
聚对苯二甲酸-共-丁二酸丁二醇酯(PBST)
3) Poly(butylene succinate-co-terephthalate)s(PBST)
聚丁二酸对苯二甲酸丁二醇酯(PBST)
4) poly(butylene succinate-co-butylene terephthalate)
聚丁二酸丁二醇-共-对苯二甲酸丁二醇酯
1.
The enzymatic degradation of poly(butylene succinate-co-butylene terephthalate) (PBST) copolyesters was studied using the lipase from Pseudomonas (Lipase PS~R).
对聚丁二酸丁二醇-共-对苯二甲酸丁二醇酯的酶解性能进行了研究。
5) CGP
聚对苯二甲酸乙二醇酯-聚对苯二甲酸丁二醇酯-聚丁二醇共聚酯
6) Poly (ethylene glycol) terephthalate-b-poly(butylene terephthalate) (PEGT-b-PBT) copoly-mer
聚乙二醇对苯二甲酸酯-b-聚对苯二甲酸丁二醇酯多嵌段共聚物
补充资料：聚[3,3-双(氟甲基)氧杂环丁烷]
分子式：
CAS号：
性质： 以氟原子取代氯的卤化聚醚树脂类似物。同氯化聚醚一样，经拉伸和极化处理的该类树脂也表现出压电和热电性质。由于分子中碳氟键的极性比碳氯键大，预期在热电性质方面具有优越性质，而且氟取代物的碳氟键能高，其化学稳定性要好于氯取代类似物。聚[3,3-双(氟甲基)氧杂环丁烷]的合成与聚[3,3-双(氯甲基)氧杂环丁烷]的制备类似，首先合成3,3-双(氟甲基)氧杂环丁烷，然后利用开环聚合反应得到该聚合物。
CAS号：
性质： 以氟原子取代氯的卤化聚醚树脂类似物。同氯化聚醚一样，经拉伸和极化处理的该类树脂也表现出压电和热电性质。由于分子中碳氟键的极性比碳氯键大，预期在热电性质方面具有优越性质，而且氟取代物的碳氟键能高，其化学稳定性要好于氯取代类似物。聚[3,3-双(氟甲基)氧杂环丁烷]的合成与聚[3,3-双(氯甲基)氧杂环丁烷]的制备类似，首先合成3,3-双(氟甲基)氧杂环丁烷，然后利用开环聚合反应得到该聚合物。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。