2) Nanopolyaniline
纳米聚苯胺
1.
This article is mainly discussed about the synthesis of nanopolyaniline in microemulsion(oil in water) consisting of four elements: dodecylbenzene sulfonic acid(DBSA) , aniline, n - butyl alcohol and water, in which DBSA served as dopant, surfactant and the source of proton, while n - butyl alcohol served as co - surfactant.
采用微乳液法制得了纳米聚苯胺,并讨论了乳化剂、氧化剂的用量对聚苯胺粒子的粒径、电导率、分子链结构等的影响。
3) PANI-NTs
聚苯胺纳米管
1.
Polyaniline nanotubes(PANI-NTs) have been prepared by a self-assembly method under acid condition and loaded with LiCl in various solvent.
采用自组装方法在酸性条件下合成了聚苯胺纳米管,并在聚苯胺纳米管上负载LiCl无机盐。
5) polyaniline nanowire
聚苯胺纳米线
1.
Oligonucleotides with phosphate groups at the 5 end were covalently linked onto amido groups of polyaniline nanowires in the presence of the water-soluble coupling reagent l-ethyl-3-(3-dimethyl- aminopropy-l)-carbodiimide (EDC).
采用电流密度递减的方法在玻碳电极表面修饰聚苯胺纳米线(PAINW),以SEM对其形貌进行表征,测得PAINW的尖端直径在80~100nm之间。
6) nmpolyanilins fiber
纳米聚苯胺纤维
1.
Develpment and use of nmpolyanilins fiber;
纳米聚苯胺纤维的开发与应用进展
补充资料:聚苯
分子式:
CAS号:
性质:又称聚对亚苯基。主链完全由对苯基连接的一类刚性链聚合物。黑色结晶,不熔不溶,难成型加工。耐高温性优良,氮气中900℃时失重率小于10%,可在300~400℃长期使用。耐辐射、耐化学腐蚀,耐摩擦,有良好的电性能。可用于恶劣条件下的化工设备和宇航方面,也可用作耐烧蚀材料。可由苯进行弗-克反应或由聚环己二烯芳构化制得,或在低分子量聚苯预聚物中加入固化剂交联成型,或烧结成型。模压烧结制品的拉伸强度6.3~13.7MPa,伸长率8%~12%。拉伸模量151MPa。体积电阻率2×1015Ω·cm。聚苯的自润滑性优于MoS2和石墨。可作为高温离子交换树脂,耐高温、耐辐照涂料及胶黏剂,高温耐磨零部件等。在苯环上引入取代基,则可降低熔融温度、改善溶解性,有利成型加工。聚苯不仅通过电化学掺杂可成为p型导电体,还因为它具有电子受体的性质,也能成为n型导电体,其电导率可达102~103S/cm。它具有可逆的氧化—还原特性,可作为蓄电池的电极材料。
CAS号:
性质:又称聚对亚苯基。主链完全由对苯基连接的一类刚性链聚合物。黑色结晶,不熔不溶,难成型加工。耐高温性优良,氮气中900℃时失重率小于10%,可在300~400℃长期使用。耐辐射、耐化学腐蚀,耐摩擦,有良好的电性能。可用于恶劣条件下的化工设备和宇航方面,也可用作耐烧蚀材料。可由苯进行弗-克反应或由聚环己二烯芳构化制得,或在低分子量聚苯预聚物中加入固化剂交联成型,或烧结成型。模压烧结制品的拉伸强度6.3~13.7MPa,伸长率8%~12%。拉伸模量151MPa。体积电阻率2×1015Ω·cm。聚苯的自润滑性优于MoS2和石墨。可作为高温离子交换树脂,耐高温、耐辐照涂料及胶黏剂,高温耐磨零部件等。在苯环上引入取代基,则可降低熔融温度、改善溶解性,有利成型加工。聚苯不仅通过电化学掺杂可成为p型导电体,还因为它具有电子受体的性质,也能成为n型导电体,其电导率可达102~103S/cm。它具有可逆的氧化—还原特性,可作为蓄电池的电极材料。