1) super-cooled liquid region
过冷液态区域
2) supercooled liquid region
过冷液态区
1.
The Ta added alloys exhibit a wide supercooled liquid region exceeding 60 K before crystallizati.
结果表明,Ta的添加提高了Ti50Ni20Cu25Sn5合金的GFA,Mo的添加降低了该合金的GFA,Nb的添加则对该合金的GFA没有明显的影响;含Ta合金具有超过60K的宽过冷液态区(ΔTx),且其约化玻璃转变温度因子(Tg/Tm)大于含Nb合金和含Mo合金;采用常规铜模铸造法制备出了直径为1mm的(Ti0。
3) super-cooled liquid state
过冷区域
4) supercooled liquid
过冷液态
1.
According to the result, the joint which will be avoided crystallizing should be in supercooled liquid with good thermal stabilization, superplasticity and viscous flow, at the same time, the temperature of the joint should always be under the crystallization temperature of the BMG.
5Ni15的连接;根据试验结果,探讨了焊接接头保持非晶的条件,即:被焊块体非晶合金处于过冷液态,且该过冷液体具有较好的热稳定性、超塑性和粘滞性,同时接触面的温度应始终低于该非晶合金的晶化温度。
2.
As a result,this can be an evidence that the transformation from the glassy state to supercooled liquid belongs to second-order transition.
利用 DSC 热分析法研究了 Zr 基及78Fe-9Si-13B 非晶合金的热容随温度的变化曲线,发现 Zr 基非晶的热容温度曲线与二级相变热容变化的规律十分相似,因此可以作为玻璃态与过冷液态之间的转变属于二级相变的一个证据。
5) supercooled liquid region
过冷液相区
1.
High strain rate compressive deformation behavior of Zr-based bulk amorphous alloy in supercooled liquid region;
Zr基非晶合金在过冷液相区的高应变速率压缩变形行为
2.
Constitutive equation for viscous flow behavior of Mg-based bulk metallic glass in supercooled liquid region;
镁基大块非晶合金在过冷液相区流变行为本构关系
3.
The forming techniques, evaluation systems and FEM application of bulk amorphous alloys in supercooled liquid region are summarized in this paper.
综述了大块非晶合金在过冷液相区微塑性成形的工艺、成形性能评价及有限元技术应用方面的研究进展。
6) zone melting and liquid metal cooling
区域熔化液态金属冷却法
补充资料：过冷
| 过冷 supercooling 温度低于凝固点但仍不凝固或结晶的液体称为过冷液体。过冷液体是不稳定的，只要投入少许该物质的晶体，便能诱发结晶，并使过冷液体的温度回升到凝固点。这种在微小扰动下就会很快转变的不稳定状态称为亚稳态。 当用适当的方式缓慢冷却饱和溶液时，可使其变成过饱和而不析出溶质的结晶，这种现象也称为过冷，这种溶液称为过冷溶液。过冷溶液也是不稳定的。 在没有尘埃、没有电荷的洁净空间中，使蒸气绝热膨胀，温度突然下降，可以不发生液化现象，而使原来的饱和蒸气变成过饱和，这种过饱和蒸气又称过冷蒸气。过冷蒸气也是不稳定的，如有微粒作凝结核心，就会出现雾滴。核物理实验技术中，利用过冷蒸气的不稳定性来产生液滴，以显示粒子的径迹，这种探测器叫做云室。 |