1) ER50-6 rod
ER50-6盘条
1.
The control cooling process of ER50-6 rod with different carbon content was studied.
通过对不同含碳量的ER50-6盘条控冷工艺研究。
2) ER50-6 wire rod
ER50-6线材
1.
To analyze the production process of ER50-6 wire rod for welding.
对生产焊接用ER50-6线材的工艺进行分析,指出冶炼后吹时间过长、吹氩时间不足、出钢温度偏高、水冷线水压不稳定等是造成线材成分不均、组织恶化、拉拔断裂的主要因素。
3) ER70S-6 wire rod
ER70S-6盘条
1.
ER70S-6 wire rod for welding breaked while drawing.
焊接用ER70S-6盘条在拉拔过程中断裂,细拉钢丝断口以杯锥状为主,粗拉钢丝断口以斜茬状为主。
4) wire rod
盘条
1.
Differentiation and identification of the pearlite structure types in carbon steel wire rod;
碳钢盘条中珠光体类型组织的区分和判定
2.
Producing stainless steel HR strip and wire rod;
不锈钢热轧带钢和盘条的生产
3.
The effect of non-metallic inclusions on drawing performance of hardening wire rod and technical controlling;
非金属夹杂物对硬线盘条拉拔性能的影响及其工艺控制
5) wire bar
盘条
1.
The trial production of ER70S-6 hot rolled wire bar is introduced.
介绍了邢钢ER70S-6热轧盘条的调试生产情况,通过采取控制化学成分、炉外处理、全程保护浇注和缓冷等措施,使盘条的化学成分达到了国标要求,拉拔性能和焊接性能满足了客户要求。
2.
The production process of pre-stressed SWRH82B wire bar in Xing Steel is introduced,its chemical composition,mechanical properties and micro-structure all meet the standard.
介绍了邢钢预应力SWRH82B盘条的生产工艺,盘条的化学成分、力学性能、显微组织等均达到了标准要求。
3.
The influence of various cooling speed on structure and property of wire bar of SCM435 cold heading steel is researched.
研究了不同冷却速度对SCM435冷镦钢盘条组织性能的影响。
6) wire rods
盘条
1.
The fractures of high carbon steel wire rods being pulled were analyzed.
针对高碳钢盘条在拉拔过程中出现的脆断问题进行了理化分析,结果表明:盘条心部存在较严重的成分偏析和脆性组织是造成高碳钢盘条脆断的主要原因。
2.
o analyze the difference between home and abroad in steel for wire rods,standard,inherent quality etc.
结合金属制品生产实际，分析国内外盘条用钢、标准、内在质量等方面存在的差异，提出了改进我国盘条质量应采取的措施。
3.
To introduce the effect of the component of low-carbon wire rods on drawing effect,property of heat-treated end product and application conditions of zinc-coated low-carbon steel wire for cotton baling,put forward the best component.
介绍低碳盘条的成分对棉花打包用低碳镀锌钢丝的拉拔效果、热处理后成品性能及产品使用情况的影响，提出最佳成分。
补充资料：[3-(aminosulfonyl)-4-chloro-N-(2.3-dihydro-2-methyl-1H-indol-1-yl)benzamide]
分子式：C16H16ClN3O3S
分子量：365.5
CAS号：26807-65-8
性质：暂无
制备方法：暂无
用途：用于轻、中度原发性高血压。
分子量：365.5
CAS号：26807-65-8
性质：暂无
制备方法：暂无
用途：用于轻、中度原发性高血压。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条