1) β-FeSi2 thermoelectric materials
β-FeSi2热电材料
3) β-FeSi_2
β-FeSi2
1.
β-FeSi_2 thin films on Si(100) by Non-mass-separated ion beam deposition(IBD) method were investigated.
作者对采用非质量分离离子束注入沉积法(IBD)在Si(100)上制备的β-FeSi2薄膜进行了研究,通过X射线衍射(XRD)和扫描电镜(SEM)以及原子力显微镜(AFM)分析表明:当退火温度在600℃和700℃附近时有利于β-FeSi2的形成。
2.
Nano-β-FeSi_2/a-Si layered structure was successfully deposited on Si(001)substrates using radio-frequency magnetron sputtering method.
采用射频磁控溅射的方法,在Si(100)基片上制备了纳米β-FeSi2/Si多层结构,利用X射线衍射、透射电子显微镜、光致发光光谱等表征技术,研究了β-FeSi2/Si多层结构的结构、成分和光致发光特性。
4) β-FeSi 2
β-FeSi2
5) Phase FeSi2
β相FeSi2
6) β-FeSi2 thin film
β-FeSi2薄膜
1.
Single-phase β-FeSi2 thin films with high quality was prepared by DC-magnetron sputtering Fe-Si mixed targets,followed by post-annealing.
本文采用室温直流磁控溅射Fe-Si组合靶的方法,并通过后续退火温度的优化得到了单一相高质量的β-FeSi2薄膜。
2.
This paper introduces the luminescent mechanism of β-FeSi2,and discusses several kinds of preparing methods for β-FeSi2 thin films.
探讨了β-FeSi2的发光机理,介绍了几种β-FeSi2薄膜制备方法并比较了不同制备方法的特点,总结了最近几年来β-FeSi2的研究进展和主要研究结果。
补充资料：聚偏二氟乙烯基热电材料
分子式：
CAS号：
性质： 聚偏二氟乙烯是具有规则头尾相接结构的结晶性聚合物，无色透明或半透明，与聚四氟乙烯相比，相对密度小、拉伸和压缩强度大，不燃、耐候性强，是氟塑料中韧性好且压电、热电性质明显的一个品种。聚偏二氟乙烯基塑料是以1,1-二氟乙烯为单体，过氧苯甲酰为催化剂，在80℃，80MPa下，经加聚反应制备；以叔丁基过氧化物催化剂，反应温度应更高些。以烷基硼衍生物作催化剂，在较低温度下聚合也可以得到高熔点的聚偏氟乙烯。聚偏氟乙烯是晶态极性聚合物，主要有α相和β相，口相主要存在于熔融的聚偏氟乙烯中，属单斜晶系，分子中总的偶极矩为零，不显示热电性；将口相的聚偏氟乙烯在120℃下拉伸4～5倍，分子链成锯齿状取向，生成卢相，属于斜方晶系，其介电常数从6～3提高到11～14，分子自发极化大，具有较高的热电性质。在拉伸的同时施加高电场，分子可以发生链旋转，提高极化度。
CAS号：
性质： 聚偏二氟乙烯是具有规则头尾相接结构的结晶性聚合物，无色透明或半透明，与聚四氟乙烯相比，相对密度小、拉伸和压缩强度大，不燃、耐候性强，是氟塑料中韧性好且压电、热电性质明显的一个品种。聚偏二氟乙烯基塑料是以1,1-二氟乙烯为单体，过氧苯甲酰为催化剂，在80℃，80MPa下，经加聚反应制备；以叔丁基过氧化物催化剂，反应温度应更高些。以烷基硼衍生物作催化剂，在较低温度下聚合也可以得到高熔点的聚偏氟乙烯。聚偏氟乙烯是晶态极性聚合物，主要有α相和β相，口相主要存在于熔融的聚偏氟乙烯中，属单斜晶系，分子中总的偶极矩为零，不显示热电性；将口相的聚偏氟乙烯在120℃下拉伸4～5倍，分子链成锯齿状取向，生成卢相，属于斜方晶系，其介电常数从6～3提高到11～14，分子自发极化大，具有较高的热电性质。在拉伸的同时施加高电场，分子可以发生链旋转，提高极化度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条