说明:双击或选中下面任意单词,将显示该词的音标、读音、翻译等;选中中文或多个词,将显示翻译。
您的位置:首页 -> 词典 -> SiC纳米棒
1)  SiC nanorod
SiC纳米棒
1.
Large-scale synthesis of SiC nanorods via periodic VLS mechanism under Fe-assisted condition
基于Fe催化条件下周期性VLS机制大量合成SiC纳米棒的研究
2)  SiC nanowires
SiC纳米线
1.
Synthesis and characterization of SiC nanowires using silicon evaporation;
硅热蒸发法制备SiC纳米线及其结构表征
2.
Formation of SiC nanowires on SiO_2 substrate by magnetron sputtering and annealing;
石英衬底上磁控溅射SiC膜退火形成SiC纳米线
3.
SiC nanowires were found in crystallochemical analysis of SiBONC ceramic powder, which was synthesized through a polymer pyrolysis route from the raw materials of tetrachloride, phenyle aldehyde, boron trichloride and aniline.
在对SiBONC陶瓷粉末坯体进行高温气压处理时,发现在坯体表面生长出大量β-SiC纳米线。
3)  nanometer SiC
纳米SiC
1.
Ni-P-SiC nanometer composite coating was prepared with electroless plating,and the effects of concentration of nanometer SiC particles in the solution on hardness of the coating were studied.
利用化学镀方法制备了Ni-P-SiC(纳米)复合镀层,研究了镀液中纳米SiC微粒含量对复合镀层硬度的影响,在MPX-2000型摩擦磨损试验机上进行了复合镀层与45钢配对的滑动磨损试验,用扫描电镜观察了磨损面的形貌。
2.
The effect of the content of the nanometer SiC particles on the microstructure and properties was discussed.
利用化学镀方法制备了Ni-P-SiC(纳米)复合镀层,研究了镀液中纳米SiC微粒的含量对复合镀层组织与性能的影响,结果表明:由于纳米SiC的加入,使复合镀时的镀速加快,原因是液固界面增加,从而增加了有效催化面积。
3.
The tribological behaviours of polyetheretherketone (PEEK) filled with nanometer SiC and micron SiC were studied.
利用热压法分别以纳米SiC和微米SiC作为填料制取了两类不同SiC填充的聚醚醚酮复合材料,并对它们在干摩擦条件下的摩擦磨损性能进行了研究,同时还用扫描电子显微镜对摩擦表面形貌进行了观察,进而对材料的磨损机理作了分析与讨论。
4)  nano-SiC
纳米SiC
1.
A study on preparation and properties of Au/nano-SiC composite coatings;
Au/纳米SiC颗粒复合镀层的制备工艺及性能
2.
Study on nano-SiC/PA66 composite;
纳米SiC/PA66复合材料的研究
3.
Preparation of Cu/nano-SiC composite powder in disproportionation reaction and replacement reaction;
歧化反应及置换反应制备Cu/纳米SiC复合粉体
5)  SiC nano-bar
SiC纳米杆
1.
Investigation of the SiC nano-bar relaxation characteristics;
SiC纳米杆的驰豫性能研究
6)  Ni-(nano)SiC
Ni-纳米SiC
补充资料:Sic

1、名称解释

碳化硅又称金钢砂或耐火砂。碳化硅是用石英砂、石油焦(或煤焦)、木屑(生产绿色碳化硅时需要加食盐)等原料在电阻炉内经高温冶炼而成。目前我国工业生产的碳化硅分为黑色碳化硅和绿色碳化硅两种,均为六方晶体,比重为3.20~3.25,显微硬度为2840~3320kg/mm2。

包括黑碳化硅和绿碳化硅,其中:黑碳化硅是以石英砂,石油焦和优质硅石为主要原料,通过电阻炉高温冶炼而成。其硬度介于刚玉和金刚石之间,机械强度高于刚玉,性脆而锋利。绿碳化硅是以石油焦和优质硅石为主要原料,添加食盐作为添加剂,通过电阻炉高温冶炼而成。其硬度介于刚玉和金刚石之间,机械强度高于刚玉。

2.性质

碳化硅的硬度很大,具有优良的导热和导电性能,高温时能抗氧化。

3.用途

(1)作为磨料,可用来做磨具,如砂轮、油石、磨头、砂瓦类等。

(2)作为冶金脱氧剂和耐高温材料。

碳化硅主要有四大应用领域,即: 功能陶瓷、高级耐火材料、磨料及冶金原料。目前碳化硅粗料已能大量供应, 不能算高新技术产品,而技术含量极高 的纳米级碳化硅粉体的应用短时间不可能形成规模经济。

(3)高纯度的单晶,可用于制造半导体、制造碳化硅纤维。

4.产地、输往国别及品质规格

(1)产地:青海、宁夏、河南、四川、贵州等地。

(2)输往国别:美国、日本、韩国、及某些欧洲国家。

(3)品质规格:

①磨料级碳化硅技术条件按gb/t2480—96。各牌号的化学成分由表6-6-47和表6-6-48给出。

②磨料粒度及其组成按gb/t2477—83。磨料粒度组成测定方法按gb/t2481—83。