2) hypoeutectic gray irons
亚共晶灰铸铁
1.
Seeing that there was so-called "C-type graphite" found by the metallographic inspection when producing small and medium size castings with HT200 or HT250 grade gray irons in some foundries, and as a result the clients refused to accept the castings, the author pointed out that C-type graphite doesn t present itself in hypoeutectic gray irons, but only in hypereutectic gray irons.
针对某些企业在生产HT200和HT250的中、小铸件时,由于金相检验认为有C型石墨存在而引起客户拒收的情况,指出C型石墨只有在过共晶灰铸铁中才会出现,不会出现在亚共晶灰铸铁中。
3) eutectic cast iron
共晶铸铁
4) hypoeutectic cast
亚共晶铸铁
5) hypereutectic cast iron
过共晶铸铁
6) Hypoeutectic High Cr Cast Iron
亚共晶高铬铸铁
1.
Microstructure of Hypoeutectic High Cr Cast Iron Prepared by Slope Plate with Different Flute Radius;
不同倾斜板凹槽半径条件下的亚共晶高铬铸铁组织
2.
Evolution of Pro-eutectic Austenite in Semi-solid Hypoeutectic High Cr Cast Iron during Remelting;
半固态亚共晶高铬铸铁重熔时先共晶相的演变
补充资料：共晶
共晶
eutectic
共晶eutectic一定成分的合金液体冷却时，转变为两种或更多紧密混合的固体的恒温可逆反应。这种反应形成的组织即为共晶组织。最简单的共晶反应是在二元合金系统中，具有共晶成分的液体L，在共晶温度下同时凝固形成两固体相a和刀共晶组织。通常用公式L禅a+刀表示。在此共晶反应温度下，出现L、a及刀三相共存。以此方式凝固的合金为共晶合金。偏离共晶成分的合金组织为亚共晶或过共晶。在冷却过程中，这些合金首先从液体中析出树枝状的先共晶组织，然后在枝晶间的液体凝固成共晶组织。可通过高的冷却速度或在液固界面高的温度梯度来抑制先共晶组织的形成，使液体可以直接通过共晶方式凝固;并可调节a及刀相的体积分量与液体的成分相适应。通常这种共晶组织又称为伪共晶。 共晶合金由于熔点低，熔化工艺相对比较简单，并且成本亦低。由于凝固的温度范围很小，改善了铸造流动性，并可抑制热缩孔、疏松及成分偏析。共晶合金具有细而分隔的多相显微组织，可以认为是具有各种特殊性能的复合材料。根据此原理，已开发出镍基和钻基共晶合金，用作抗蟠变材料，可制作喷气发动机叶片。 (汪复兴)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条