1) PVDF
聚偏氟乙烯(PVDF)
1.
Polyvinylidene fluoride(PVDF) membrane was made by N,N-dimethylformamide(DMF) as the solvent and fluoride resin as the hydrophobic agent.
采用N,N-二甲基甲酰胺(DMF)为溶剂,以氟树脂为疏水助剂,制备聚偏氟乙烯(PVDF)膜。
2.
The modified method of water vapor induced membrane formation was introduced to prepare high hydrophobic poly(vinylidene fluoride)(PVDF) porous membrane in this paper.
采用改进的水蒸气(或称水雾蒸气)诱导成膜的方法制备强疏水性的聚偏氟乙烯(PVDF)微孔膜。
2) poly(vinylidene fluoride) (PVDF)
聚偏二氟乙烯 PVDF
3) Poly(vinylidene fluoride)(PVDF)
聚偏二氟乙烯(PVDF)
1.
Poly(vinylidene fluoride)(PVDF) is the fluoro-plastics which has the best properties of piezoelectric material in practical applications.
聚偏二氟乙烯(PVDF)是目前实际应用中压电性能最好的含氟塑料。
4) poly(vinylidene difluoride)
聚偏氟二乙烯(PVDF)
5) PVDF piezoelectric-film
聚偏氟乙烯(PVDF)压电薄膜
6) polyvinyliene fluoride sensors
聚偏氟乙烯(PVDF)传感器
补充资料：聚偏氟乙烯
[-CH2-CF2-]-
白色粉末状结晶性聚合物。密度1．75-1．78g／cm3。玻璃化湿度-39℃，脆化温度-62℃，熔点170℃， 热分解温度316℃以上，长期使用温度－40～150℃。可用一般热塑性塑料加工方法成型。其突出特点是机械强度高，耐辐照性好。具有良好的化学稳定性，在室温下不被酸、碱、强氧化剂和卤素所腐蚀，发烟硫酸、强碱、酮、醚绵少数化学药品能使其溶胀或部分溶解，二甲基乙酰胺和二甲基亚砜等强极性有机溶剂能使其溶解成胶体状溶液。
拉伸强度 (MPa) ＞ 40
应用领域 用于制作化工机械零件。密封材料，电线电缆包覆层，接线板，印刷电路板，电绝缘及防腐涂层。还可用于制备离子交换膜及电容器薄膜等材料。也用于锂离子电池内极片的粘结剂。
白色粉末状结晶性聚合物。密度1．75-1．78g／cm3。玻璃化湿度-39℃，脆化温度-62℃，熔点170℃， 热分解温度316℃以上，长期使用温度－40～150℃。可用一般热塑性塑料加工方法成型。其突出特点是机械强度高，耐辐照性好。具有良好的化学稳定性，在室温下不被酸、碱、强氧化剂和卤素所腐蚀，发烟硫酸、强碱、酮、醚绵少数化学药品能使其溶胀或部分溶解，二甲基乙酰胺和二甲基亚砜等强极性有机溶剂能使其溶解成胶体状溶液。
拉伸强度 (MPa) ＞ 40
应用领域 用于制作化工机械零件。密封材料，电线电缆包覆层，接线板，印刷电路板，电绝缘及防腐涂层。还可用于制备离子交换膜及电容器薄膜等材料。也用于锂离子电池内极片的粘结剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。