1) hole area ratio
开孔面积比
2) pore specific surface area
孔比表面积
1.
Effect of the perlite admixture on the pore structure, such as porosity, median pore diameter, pore specific surface area, and pore size distribution was analyzed and discussed.
为探讨珍珠岩掺合料对水泥基材料性能影响的机理,用压汞法测试掺加质量分数为0～40%珍珠岩掺合料水泥石的微孔结构参数,分析珍珠岩掺合料对3,28,60d龄期水泥石孔结构参数:孔隙率、中值孔径、孔比表面积和孔级配的影响。
3) crack area ratio
孔隙面积比
1.
The gray images of cracking of specimen with different water content are analyzed by digital image technique in dynamic deformation process,and the relationships of crack area ratio,strain,and water content are also obtained.
为了研究红砂岩的初始损伤效应,对红砂岩进行细观损伤单轴压缩试验,同步多方位观测细观裂纹演化过程,利用数字图像相关技术处理不同含水率下红砂岩试样动态变形过程中灰度分布图,得到孔隙面积比、应变以及含水率之间的相互关系;探讨孔隙面积比与损伤变量之间的联系,进而推导了红砂岩损伤变量随含水率变化的计算公式,定量评价不同含水率下红砂岩的初始损伤程度。
4) open area ratio
开口面积比
1.
The method of improving the open area ratio and reducing the noise of MCP from enlarging the input end of the channel is presented.
提出对微通道板输入表面采用扩口技术提高微通道板的开口面积比,从而降低微通道板噪声的方法。
5) expanded area ratio
展开面积比
6) specific surface area of porous calcium oxide
多孔CaO比表面积
补充资料：开孔
分子式：
CAS号：
性质：(一)open pore 孔性固体中与外界连通的空腔和孔道称为开孔。不与外界连通的称为闭孔(close pore)。开孔与闭孔大多为孔性固体制备过程中形成的，有时也可在后处理过程中形成，如高温烧结可使开孔变为闭孔。(二)open cell 在软质聚氨酯泡沫塑料生产中，发泡过程后期，由于膜壁黏度较大，无法流动，同时弹性较低，无法承受膜壁的拉伸，从而造成气泡破裂，使气体逸出，这种现象称之为开孔。最有效的方法是调整催化剂或加开孔剂提高开孔率，将其混合在物料体系中，在泡沫塑料成型过程中影响体系表面张力，在适当的时候促使泡孔开孔化，防止制品收缩，改善柔性，提高制品的尺寸稳定性。其品种较多，可分为有机化合物、无机化合物和低分子量聚合物，如多胺，某些有机硅化合物，硝酸锆，多官能低分子量聚醚，低分子量聚苯乙烯等。也可采用机械方法开孔，开孔率高，软泡的回弹好。
CAS号：
性质：(一)open pore 孔性固体中与外界连通的空腔和孔道称为开孔。不与外界连通的称为闭孔(close pore)。开孔与闭孔大多为孔性固体制备过程中形成的，有时也可在后处理过程中形成，如高温烧结可使开孔变为闭孔。(二)open cell 在软质聚氨酯泡沫塑料生产中，发泡过程后期，由于膜壁黏度较大，无法流动，同时弹性较低，无法承受膜壁的拉伸，从而造成气泡破裂，使气体逸出，这种现象称之为开孔。最有效的方法是调整催化剂或加开孔剂提高开孔率，将其混合在物料体系中，在泡沫塑料成型过程中影响体系表面张力，在适当的时候促使泡孔开孔化，防止制品收缩，改善柔性，提高制品的尺寸稳定性。其品种较多，可分为有机化合物、无机化合物和低分子量聚合物，如多胺，某些有机硅化合物，硝酸锆，多官能低分子量聚醚，低分子量聚苯乙烯等。也可采用机械方法开孔，开孔率高，软泡的回弹好。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。