1) eutectic ceramics
共晶陶瓷
1.
The high temperature eutectic ceramics have been fabricated by combustion synthesis melt casting under ultra-high gravity field.
研究以超重力辅助燃烧合成熔融铸造方法快速制备超高温氧化物共晶陶瓷,即,以Al/NiO/Y2O3/ZrO2为反应剂,通过诱发各组元间的燃烧合成反应,首先获得陶瓷和金属的混合熔体,随后利用2种熔体的密度差异,在超重力场中实现陶瓷熔体和金属熔体的彻底分离和凝固,成功制备了Al2O3、钇铝石榴石(yttrium aluminumgarnet,YAG)、Y稳定ZrO2(yttria-stabilized zirconia,YSZ)共晶陶瓷块体材料Al2O3/YAG/YSZ。
2) eutectic ceramics rod
共晶陶瓷棒体
1.
According to the strong constraining feature of interfaces of microstrctures,the micromechanical stress field in an eutectic ceramics rod was determined through the shear stress along fiber-matrix interfaces.
根据细观结构内界面的强约束特性,通过纤维-基体内界面切应力确定了共晶陶瓷棒体的细观应力场。
3) eutectic ceramic in-situ composite
共晶自生复合陶瓷
1.
Laser rapid remelting experiments were conducted on the preparation of Al2O3/YAG eutectic ceramic in-situ composite to investigate the microstructure characteristic and growth behavior under an ultra-high temperature gradient and different laser scanning rates of 0.
采用激光快速熔凝技术制备Al2O3/YAG共晶自生复合陶瓷,研究Al2O3/YAG共晶陶瓷在高能激光束作用下,不同扫描速率(0。
4) Al2O3/YSZ eutectic composite ceramics
Al2O3/YSZ共晶复合陶瓷
5) Al2O3/ZrO2(Y2O3) eutectic composite ceramics
Al2O3/ZrO2(Y2O3)共晶复合陶瓷
6) super refractory material
陶瓷共晶复合材料
补充资料：共晶
共晶
eutectic
共晶eutectic一定成分的合金液体冷却时，转变为两种或更多紧密混合的固体的恒温可逆反应。这种反应形成的组织即为共晶组织。最简单的共晶反应是在二元合金系统中，具有共晶成分的液体L，在共晶温度下同时凝固形成两固体相a和刀共晶组织。通常用公式L禅a+刀表示。在此共晶反应温度下，出现L、a及刀三相共存。以此方式凝固的合金为共晶合金。偏离共晶成分的合金组织为亚共晶或过共晶。在冷却过程中，这些合金首先从液体中析出树枝状的先共晶组织，然后在枝晶间的液体凝固成共晶组织。可通过高的冷却速度或在液固界面高的温度梯度来抑制先共晶组织的形成，使液体可以直接通过共晶方式凝固;并可调节a及刀相的体积分量与液体的成分相适应。通常这种共晶组织又称为伪共晶。 共晶合金由于熔点低，熔化工艺相对比较简单，并且成本亦低。由于凝固的温度范围很小，改善了铸造流动性，并可抑制热缩孔、疏松及成分偏析。共晶合金具有细而分隔的多相显微组织，可以认为是具有各种特殊性能的复合材料。根据此原理，已开发出镍基和钻基共晶合金，用作抗蟠变材料，可制作喷气发动机叶片。 (汪复兴)