2) hydrothermal modification
水热改性
1.
Effect of hydrothermal modification conditions on preparation of flame retardant Mg(OH)_2 in large-scale experimental set-up;
水热改性条件对制备氢氧化镁阻燃剂中试研究的影响
2.
Preparation of dispersive zinc oxide nano-particles via hydrothermal modification route
水热改性法制高分散纳米氧化锌工艺初探
3.
The hydrothermal modification behavior of industrial Mg(OH)_(2) products in a new additive solution was researched.
研究了氢氧化镁工业品在一种新型添加剂作用下的水热改性行为,考察了添加剂体系、反应温度、反应时间、添加剂浓度和填充度等因素对水热产物的影响,并用扫描电子显微镜(SEM)、X射线衍射(XRD)和激光粒度仪等对水热产物进行了表征。
3) Hot water modification
热水改性
4) phosphorus and steam modification
磷和水蒸气改性
5) hydrothermal modification treatment
水热改性处理
1.
In order to solve the problem that the Mg(OH)_2 is incompatible with the polymer,the two steps reaction of high dispersive Mg(OH)_2 preparation,synthetic reaction and hydrothermal modification treatment,was studied.
为了解决氢氧化镁和聚合物之间的不相容问题,对氨合成法-水热改性处理2步法制备高分散氢氧化镁阻燃剂进行了研究,分析了常温合成温度、水热改性温度和水热改性时间对制备大晶型、低比表面积氢氧化镁阻燃剂的影响。
6) Property improvement calcium phosphate cement
改性磷酸钙骨水门汀