1) NiZnCo-ferrite
镍锌钴铁氧体
1.
Study on Low-temperature Hydrothermal Synthesis and High-frequency Electromagnetic Properties of NiZnCo-ferrite
镍锌钴铁氧体的水热低温合成与高频电磁性能研究
2) cobalt nickel ferrite
钴镍铁氧体
3) Ni-Co ferrite
镍钴铁氧体
1.
Nano Co composite Ni-Co ferrite radar wave absorber was used to prepare single layer coating,and two layers made by carbonyl + nano Co composite Ni-Co ferrite were also prepared.
以纳米铁酸镍钴铁氧体复合Co粉、羰基铁粉等为吸收剂,并采用化学镀层,进行了单层、双层和三层涂层的试验研究。
6) Ni-Zn ferrite
镍锌铁氧体
1.
Preparation of Ni-Zn ferrite from sodium jarosite residue;
用黄钠铁矾渣制备复合镍锌铁氧体
2.
The relationship between magnetization differential and temperature in Ni-Zn ferrite;
镍锌铁氧体微分磁化率与温度的关系
3.
The relations of magnetization differential with magnatic intensity describedby dM/dt-H curves are studied in Ni-Zn ferrite with a constant rate of increasing H.
用匀速率增加的直流磁场Ｈ磁化不同居里温度的镍锌铁氧体试样，测得磁化强度Ｍ的时间变化率曲线表明：同一温度下随外场速率Ｈ增加，曲线升高；同一外场速率下随温度升高，曲线降低；微分磁化率ｄＭ／ｄＨ可以采用等效畴壁运动表示。
补充资料：锂.镍矩磁铁氧体
分子式：
CAS号：
性质：以锂、镍和铁的氧化物为主要成分的一种宽温矩磁铁氧体材料。化学式(Li2O，NiO，ZnO)Fe2O3。密度4.8g/cm3。居里温度300～400％。开关速度快，开关系数(0.557～11.94)×10-6A·S/m。体积电阻率5×10-4Ω·cm。温度稳定性好。但矩形比稍低。采用电子陶瓷工艺，1000℃以上高温，在空气、氧气或氮气气氛中烧结而成。主要用作高速度、大容量电子计算机的存贮元件。是用量较大的铁氧体材料之一。
CAS号：
性质：以锂、镍和铁的氧化物为主要成分的一种宽温矩磁铁氧体材料。化学式(Li2O，NiO，ZnO)Fe2O3。密度4.8g/cm3。居里温度300～400％。开关速度快，开关系数(0.557～11.94)×10-6A·S/m。体积电阻率5×10-4Ω·cm。温度稳定性好。但矩形比稍低。采用电子陶瓷工艺，1000℃以上高温，在空气、氧气或氮气气氛中烧结而成。主要用作高速度、大容量电子计算机的存贮元件。是用量较大的铁氧体材料之一。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。