1) TiO2 spherical micro particles
TiO2微球
1.
Using hydrothermal method without templates,brookite TiO2 spherical micro particles are successfully synthesized whose diameter sizes are 300~800nm.
采用水热法在不使用模板剂的条件下合成了在水中分散良好、粒径为300～800nm、规则的锐钛矿型TiO2微球。
2) hollow TiO2 microspheres
空心TiO2微球
1.
After removing the PS colloidal crystal template,ordered arrays of hollow TiO2 microspheres were formed.
当利用煅烧的方法去除PS胶粒晶体模板后,可以形成空心TiO2微球的三维有序排列。
3) TiO2 hollow sphere
TiO2空心球
1.
Using colloidal TiO2 from titanium tetrachloride as the precursor, and polystyrene (PS) beads as templates, nanostructure TiO2 composite and TiO2 hollow spheres were successfully prepared by the surfac- tant-assisted route and the technique of layer-by-layer self-assembly.
以TiCl4的盐酸溶液配制的TiO2溶胶为前驱体,以聚苯乙烯微球为载体,在表面活性剂存在下,通过逐层自组装技术制备了纳米结构TiO2/PS及TiO2空心球。
4) Spherical TiO2
球形TiO2
1.
The results of the experiments show that the spherical TiO2 with narrow size distribution and nice dispersibility can be obtained at the optimal RH ratio and the optimal surfactant concentration by hydrolysis of industrial TiOSO4.
在水和正丙醇的混合溶剂体系中水解工业TiOSO4成功制备得到了球形TiO2,制得的二氧化钛具有粒径分布窄、分散性好的优点。
5) ultrafine TiO_2
超微细TiO2
1.
A study on kinetics of AGD destruction by ultrafine TiO_2 photocatalysis;
对用超微细TiO2光催化酸性粒子元青的降解动力学进行了研究。
6) Colloidal TiO2
TiO2超微粒
补充资料：Tio2
钛的氧化物——二氧化钛，是雪白的粉末，是最好的白色颜料，俗称钛白。以前，人们开采钛矿，主要目的便是为了获得二氧化钛。钛白的粘附力强，不易起化学变化，永远是雪白的。特别可贵的是钛白无毒。它的熔点很高，被用来制造耐火玻璃，釉料，珐琅、陶土、耐高温的实验器皿等。
二氧化钛是世界上最白的东西， l克二氧化钛可以把 450多平方厘米的面积涂得雪白。它比常用的白颜料一—锌钡白还要白5倍，因此是调制白油漆的最好颜料。世界上用作颜料的二氧化钛，一年多到几十万吨。二氧化钛可以加在纸里，使纸变白并且不透明，效果比其他物质大10倍，因此，钞票纸和美术品用纸就要加二氧化钛。此外，为了使塑料的颜色变浅，使人造丝光泽柔和，有时也要添加二氧化钛。在橡胶工业上，二氧化钛还被用作为白色橡胶的填料。