4) hollow fibrous nickel plaque
中空纤维镍基板
1.
To suitably control impregnation time and improve the quality of impregnation,kinetics of weight gain in impregnation process of hollow fibrous nickel plaque were investigated by electrochemical impregnation and special electrochemical impregnation.
为合理控制浸渍时间和提高浸渍质量,在实验室研究的基础上,对中空纤维镍基板的电化学浸渍和特殊电化学浸渍的增重动力学进行了探讨,分析了浸渍过程机制,提出了浸渍过程动力学的三段控速机制,即化学反应-化学反应与扩散混合-扩散控速,并推导出了其数学表达式。
2.
Based on the amount of preparation work of hollow fibrous nickel plaque in laboratory, ANN-GA programs on computer network which were designed by our group was used in optimizing the process parameters and looking for the optimized condition.
在实验室研究中空纤维镍基板的制备工艺的基础上,采用自制的网络化的ANN-GA系统对58个样本进行了工艺参 数优化和寻优,得到的最佳工艺参数如下:中空镍纤维含量为97％;烧结温度为1275 K;保温时间为20 min;造孔剂PVB, PP和Ni(OH)2的含量分别为5％,3。
5) middlelength fiber
中长纤维毡
6) hollow nickel fiber Ni Cd cell
中空纤维镉镍电池
补充资料：丙烯腈-醋酸乙烯共聚物超细纤维毡
分子式：
CAS号：
性质：用静电纺丝法等制得的丙烯腈-醋酸乙烯共聚物超细纤维毡片。平均直径0.8μm，不匀率45％。制法是将该共聚物溶于二甲基甲酰胺中配成浓度20％的纺丝原液，在5kV电压及30cm带电距离下连续进行静电纺丝并接受成毡而得。用作精密过滤等滤材。
CAS号：
性质：用静电纺丝法等制得的丙烯腈-醋酸乙烯共聚物超细纤维毡片。平均直径0.8μm，不匀率45％。制法是将该共聚物溶于二甲基甲酰胺中配成浓度20％的纺丝原液，在5kV电压及30cm带电距离下连续进行静电纺丝并接受成毡而得。用作精密过滤等滤材。