1) FeNiTi/Cr_3C_2 coatings
FeNiTi/Cr3C2涂层
1.
The results show that the microstructure of FeNiTi/Cr_3C_2 coatings consists of Cr,Ti,Fe-Ni solid solution,oxides phases and intermetallics.
结果表明:FeNiTi/Cr3C2涂层基体相结构为含Cr、Ti元素的Fe-Ni基固溶体;添加纳米TiC可以明显提高涂层的硬度、内聚强度和结合强度;涂层表现出了良好的抗热腐蚀性能,腐蚀时间超过50h,达到20钢的15倍;添加纳米TiC的FeNiTi/Cr3C2涂层具有优良的抗高温冲蚀性能。
2) Fe-Al/Cr_3C_2 coating
FeAl/Cr3C2涂层
3) NiCr-Cr_3C_2 coating
NiCr-Cr3C2涂层
4) Cr3C2-NiCr coating
Cr3C2-NiCr涂层
1.
This paper investigated the effect of fuel flow on microstructure and erosion performance with the flow rate of O2 and spraying distance maintained constant,and discussed erosion angle affect on the erosion wear performance of Cr3C2-NiCr coatings.
在氧气流量和喷涂距离一定的条件下,揭示了燃气流量对超音速火焰喷涂Cr3C2-NiCr涂层显微结构及冲蚀性能的影响,并探讨了冲蚀角度对Cr3C2-NiCr涂层冲蚀性能的影响。
2.
Cr3C2-NiCr coating was deposited on 2Cr10MoVNbN steel substrate by detonation spraying method.
采用爆炸喷涂方法在2Cr10MoVNbN钢基体表面制备了Cr3C2-NiCr涂层,利用光学显微镜、扫描电镜、X射线衍射仪、能谱仪、显微硬度计、电子拉伸试验机、X射线应力仪、疲劳试验机等分析测试了涂层的缺陷、显微硬度、断裂韧度、结合力、残余应力、疲劳性能等,主要研究了涂层对基体疲劳性能的影响。
5) Cr3C2-25NiCr coating
Cr3C2–25NiCr涂层
6) FeMnCr/Cr_3C_2 coating
FeMnCr/Cr3C2涂层
1.
FeMnCr/Cr_3C_2 coatings on 20 steel substrate were prepared by high velocity arc spraying.
采用高速电弧喷涂技术在20钢表面制备了FeMnCr/Cr3C2涂层。
补充资料：[3-(aminosulfonyl)-4-chloro-N-(2.3-dihydro-2-methyl-1H-indol-1-yl)benzamide]
分子式：C16H16ClN3O3S
分子量：365.5
CAS号：26807-65-8
性质：暂无
制备方法：暂无
用途：用于轻、中度原发性高血压。
分子量：365.5
CAS号：26807-65-8
性质：暂无
制备方法：暂无
用途：用于轻、中度原发性高血压。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条