1) scratch-resistant property
耐刮擦性能
2) erasing quality
耐擦性能
3) scratch-resistant
耐刮擦
1.
The mechanical properties and scratch-resistant properties of PC/ABS alloys could be improved obviously by adding nano-MgO particles.
添加纳米MgO后的PC/ABS合金与纯PC/ABS空白样相比,其拉伸、弯曲和缺口冲击强度及表面耐刮擦性能都得到了明显改善,其中合金弯曲强度可提高20%,缺口冲击强度可提高77。
2.
The scratch-resistant SiO2 antireflective coatings were prepared by dipping of the glass followed by a thermal curing at 700 ℃ taking place simultaneously with the glass toughening, using the base/acid two-step catalytic sol-gel process with tetraethylorthosilicate (TEOS) as precursor.
17％,在400-800nm的波长范围内平均反射率较镀膜前下降了5％以上,同时薄膜具有较好的耐刮擦性能。
4) image-smudge resistance
耐摩擦性能
1.
This paper introduced several test methods of image-smudge resistance of carbonless copy paper,and did some comparion and discussison on the testing results.
本文介绍了无碳复写纸耐摩擦性能的几种评价方法,并对检测结果进行了比较和分析探讨。
5) scratch resistance
耐刮伤性
1.
After being added in the wood coatings,the wax particles were homodispersed in the coating films,which could improve the tackiness resistance and the scratch resistance of coating films.
采用复配法将水性蜡助剂加入到水性木器涂料中,蜡助剂在涂料成膜时均匀地分散在整个涂层中,蜡助剂的加入能够显著提高漆膜的抗回粘性和耐刮伤性能,但是大粒径的蜡助剂会引起漆膜光泽的下降。
2.
The morphology and structure of the nanocomposite coatings were characterized by transmission electron microscopy(TEM) and small angle X-ray scattering(SAXS) method,while the scratch resistance by the gloss loss of the coatings film after washing.
以四乙氧基硅烷(TEOS)作为主要前驱体,通过改变溶胶-凝胶工艺参数制得了结构和形态各异的丙烯酸酯聚氨酯/SiO2纳米复合涂层,利用TEM、SAXS等手段表征涂层的结构与形态,由洗刷前后涂层的失光率来表征耐刮伤性,详细探讨了纳米复合涂层耐刮伤性与SiO2相特征、有机无机相作用力及SiO2质量分数之间的关系。