Sol-gel process of silica alkoxide was performed in solution of poly(ethylene oxide) dissolved in dimethyl formamide(DMF) to limit the sites of hydrolysis and dehydration-condensation of alkoxide(tetraethyl orthosilicate(TEOS)) to the inside of the dispersed droplets and to prepare silica particles of several μm in diameter.
利用sol-gel法,通过正硅酸乙酯(tetraethyl orthosilicate(TEOS))在聚氧化乙烯/二甲基甲酰胺溶液中水解、缩聚,制备了粒径分布均匀的微米级二氧化硅粒子;利用扫描电子显微镜观测了制备条件对二氧化硅粒子的粒度和形貌的影响;研究了这一方法在制备无机粒子过程中的原理。
4) silica seed
二氧化硅种子
5) silica for electronic grade
电子级二氧化硅
6) monodisperse silica
单分散二氧化硅
1.
Two monodisperse silica latex systems with 173nm and 297 nm in diameter were fabricated with controlled growth method and tetraethyllorthosilicate as its materials.
以正硅酸乙酯为原料,采用控制凝聚法制备出173nm和297nm两种不同粒径的单分散二氧化硅微球乳液,并在一定湿度和温度下,利用乳液的单分散性,在表面张力的驱使下完成微球的自组装,从而得到三维有序的二氧化硅胶态晶体。
2.
Monodisperse silica spheres were prepared by hydrolysis and condensation of tetraethoxysilane (TEOS) in a mixture of water, ammonia and ethanol or acetone at 25℃.
单分散二氧化硅是指尺寸分布十分狭窄的二氧化硅颗粒。
补充资料:大分子单体
分子式:
CAS号:
性质:简称大单体。带有可聚合端基的线型聚合物,一般分子量在1000~2000左右,分子量分布窄。可由负离子聚合、正离子聚合、基团转移聚合、自由基聚合及缩聚等制备。可聚合端基有苯乙烯基、烯丙基、甲基丙烯酰基、环氧基、噁唑啉基等。大分子单体与一般单体共聚,可得到支链长短很规整的接枝共聚物。大分子单体的共聚物或均聚物常被称为梳状聚合物。
CAS号:
性质:简称大单体。带有可聚合端基的线型聚合物,一般分子量在1000~2000左右,分子量分布窄。可由负离子聚合、正离子聚合、基团转移聚合、自由基聚合及缩聚等制备。可聚合端基有苯乙烯基、烯丙基、甲基丙烯酰基、环氧基、噁唑啉基等。大分子单体与一般单体共聚,可得到支链长短很规整的接枝共聚物。大分子单体的共聚物或均聚物常被称为梳状聚合物。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条