1) slit-extrusion-hot-stretching-quenching process
熔融挤出-热拉伸-淬冷法
2) melting extrusion-hot stretching-quenching technique
熔融挤出-热拉伸-淬冷
1.
The in-situ microfiber-contained polymer blend (MCB) based on poly (ethylene terephthalate) (PET) and polyethylene (PE) was prepared through melting extrusion-hot stretching-quenching technique in a single screw extruder with a rectangular slit die.
用“熔融挤出-热拉伸-淬冷”方法制备了聚对苯二甲酸乙二醇酯(PET)/聚乙烯(PE)原位微纤化共混物(MCB),研究了热拉伸比恒定时组成对MCB形态和力学性能的影响。
3) melt-quenching method
熔融-淬冷法
1.
1CsBr glasses were prepared by conventional melt-quenching method.
用熔融-淬冷法制备了无稀土掺杂与Dy~(3+)(0。
4) melt quenching method
熔融淬冷法
1.
Vanadium pentoxide xerogel ( VXG) films electrodes used for lithium rechargeable batteries were prepared from crystalline vanadium pentoxide ( c-V2O5) by melt quenching method, then the basic shape of the EIS of VXG films electrodes were described.
以晶态V2O5(c-V2O5)为原料,采用熔融淬冷法成功制取了V2O5干凝胶(VXG)薄膜电极,研究了该电极电化学阻抗谱(EIS)的基本形状及其随电位的变化,并用等效电路拟合了不同电位下的EIS,同时系统地测试分析了与电极材料性质和电极荷电状态相联系的一些参数。
2.
Vanadium pentoxide xerogel (VXG) films electrodes used for lithium rechargeable batteries were prepared from crystalline vanadium pentoxide (c-V2O5) by melt quenching method, then the basic shape of the EIS of VXG films electrodes were described.
以晶态V2O5(c-V2O5)为原料,采用熔融淬冷法成功制取了V2O5干凝胶(VXG)薄膜电极,研究了该电极EIS的基本形状及其随电位的变化,并用等效电路拟合了不同电位下的EIS,同时系统地测试分析了与电极材料性质和电极荷电状态相联系的一些参数。
5) melt-spinning-cold stretching method
熔融纺丝-拉伸法
1.
solution spinning method,melt-spinning-cold stretching method(MSCS) and thermally induced phase separation method(TIPS) are introduced in this article.
介绍了中空纤维膜3种主要制备方法,即溶液纺丝法、熔融纺丝-拉伸法和热致相分离法。
6) melt stretch
熔融拉伸
1.
Phase separation(nonsolvent induced phase separation,spreading solution on water surface and so on),melt stretch,thermally induced phase separation are included.
本文对聚4-甲基-1-戊烯微孔膜的成膜方法进行了综述,主要有相转化法,包括非溶剂致相转化法、溶剂蒸发成膜法、高分子溶液的水面展开法;熔融拉伸法;热致相分离法及其衍生法。
补充资料：熔融
分子式：
CAS号：
性质：温度升高时，分子的热运动能增大，导致结晶破坏，物质由晶相变为液相的过程。熔融是一级相转变，熔融有热焓、熵和体积的增大。发生熔融的温度叫熔点或熔融温度。小分子晶体的熔点温度范围很窄（一般小于1℃），而聚合物由于结晶不完全；其熔融温度往往是一个较宽的范围（一般为10～20℃）。
CAS号：
性质：温度升高时，分子的热运动能增大，导致结晶破坏，物质由晶相变为液相的过程。熔融是一级相转变，熔融有热焓、熵和体积的增大。发生熔融的温度叫熔点或熔融温度。小分子晶体的熔点温度范围很窄（一般小于1℃），而聚合物由于结晶不完全；其熔融温度往往是一个较宽的范围（一般为10～20℃）。