1) χphase
χ相
1.
But subjected to"aging"treatments at temperatures of 600 to 1000℃,duplex stainless steels will precipitate a certain amount of intermetallic phases such asσphase,χphase and chromium nitride,etc.
结果表明,固溶后经时效处理,金属间相在铁素体内和铁素体/奥氏体晶界析出;650℃时效时,析出的金属间相主要是χ相;750℃时效时析出σ相和χ相,此时σ相由χ相演变而来;850℃时效下则直接析出σ相;950℃时效后,少量的σ相仅在铁素体/奥氏体晶界产生。
2) χ-parameter
χ(相互作用)参数
3) tail association measureχ
尾部相关性度量χ
1.
We calculate the correlation coefficient Kendallτ,Spearmanρand the tail association measureχ.
计算了其Kendall相关系数τ,Spearman相关系数ρ和尾部相关性度量χ。
4) χ-Fe_5C_2
χ-Fe5C2
1.
It is identified that there exist all kinds of carbides similar to those of high carbon tempering martensite,that is,the appearance of carbides η-Fe_2C,χ-Fe_5C_2 were discovered in lower bainite transformation and the carbides could precipitate in two kinds of orders : the first in complicated process of η(ε)→χ→θ and the second in simple way of ε→θ.
研究证实:有类似高碳马氏体回火转变的各类碳化物,发现在转变中有η-Fe2C及χ-Fe5C2相碳化物出现;碳化物有η(ε)→χ→θ的复杂析出贯序,并且与ε→θ的简单析出贯序并存,显示基体碳偏聚即贝氏体预相变的结果。
5) thermodynamic interaction parameter χ'23
热力学相互作用参数χ'_(23)
6) X-T curve
χ-T曲线
补充资料：χ2检验χ2-test
分子式：
CAS号：
性质：又称卡方检验。假设检验是统计推断的基本内容，它的任务是利用样本提供的信息，对总体分布是否具有指定特征作出判断。其中检验统计量是否服从χ2分布的检验方法即称为χ2检验或卡方检验。它是处理测试数据的一种常用方法，在分析测试中有着广泛的应用。
CAS号：
性质：又称卡方检验。假设检验是统计推断的基本内容，它的任务是利用样本提供的信息，对总体分布是否具有指定特征作出判断。其中检验统计量是否服从χ2分布的检验方法即称为χ2检验或卡方检验。它是处理测试数据的一种常用方法，在分析测试中有着广泛的应用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条